直流电流对Cu-0.33Cr-0.06Zr合金导电性的影响
Influence of Direct Current Intensity on Electrical Conductivity of Aged Cu-0.33Cr-0.06Zr Alloy
2014年34卷第5期页码：556-558
纸质出版日期： 2014 ，
DOI： 10.15980/j.tzzz.2014.05.024

扫描看全文

[1]白宁,张彦敏,汪美珍,宋克兴,乔艳艳.直流电流对Cu-0.33Cr-0.06Zr合金导电性的影响[J].特种铸造及有色合金,2014,34(05):556-558.

Bai Ning, Zhang Yanmin, Wang Meizhen, et al. Influence of Direct Current Intensity on Electrical Conductivity of Aged Cu-0.33Cr-0.06Zr Alloy[J]. Special Casting & Nonferrous Alloys, 2014,34(5):556-558.
[1]白宁,张彦敏,汪美珍,宋克兴,乔艳艳.直流电流对Cu-0.33Cr-0.06Zr合金导电性的影响[J].特种铸造及有色合金,2014,34(05):556-558. DOI： 10.15980/j.tzzz.2014.05.024.

Bai Ning, Zhang Yanmin, Wang Meizhen, et al. Influence of Direct Current Intensity on Electrical Conductivity of Aged Cu-0.33Cr-0.06Zr Alloy[J]. Special Casting & Nonferrous Alloys, 2014,34(5):556-558. DOI： 10.15980/j.tzzz.2014.05.024.

摘要

对Cu-0.33Cr-0.06Zr合金在450℃下进行不同时效时间及不同电流密度的时效试验。研究了不同电流密度对Cu-0.33Cr-0.06Zr合金时效后电导率的影响。结果表明

在相同时效温度与时间的条件下

合金在电流密度为100A·cm-2的合金电导率低于无电流时效的;而电流密度为400A·cm-2的合金电导率高于无电流时效的。随着电流密度增加

合金的电导率有先下降再上升的趋势。在电流密度为400A·cm-2下时效2h后合金的电导率达到49.53 MS/m

与无电流时效6h相当。说明较大密度的直流电流可以加速溶质元素的析出

大大提高析出效率。

Abstract

Cu-0.33Cr-0.06Zr alloy was treated by solid solution treatment

cold deformation and aged with different aging time and different current intensities at 450℃to understand the effects of different DC current intensities on electric conductivity of the alloy aged.The results show that compared with the alloy aged without DC current

the electric conductivity of the alloy aged with 100A/cm2 DC current is lower

while the one aged with 400A/cm2 DC current is higher with a fixed aging temperature and time.The electric conductivity of the alloy aged is firstly decreased and then increased with the increase of current intensity at a given aging time.With 400A/cm2 DC current

the electrical conductivity of alloy with aged for 2hours is increased to 49.53MS/m

equivalent to the alloy aged 6hours without DC current.The results reveal that high current intensity can promote the precipitation of solute element and improve the efficiency of precipitation greatly

which are attributed to co-action of the Joule heating and electron wind force to vacancies and dislocation.