挤压态AM30镁合金高速冲击载荷下的断裂形貌分析
Failure Mode and Fracture Morphology Analysis of Extruded AM30 Magnesium Alloy under High Strain Rate Loading
2013年33卷第3期页码：204-208
纸质出版日期： 2013 ，
DOI： 10.15980/j.tzzz.2013.03.012

扫描看全文

[1]王怀国,毛萍莉.挤压态AM30镁合金高速冲击载荷下的断裂形貌分析[J].特种铸造及有色合金,2013,33(03):204-208.

Wang Huaiguo1, Mao Pingli2. Failure Mode and Fracture Morphology Analysis of Extruded AM30 Magnesium Alloy under High Strain Rate Loading[J]. Special Casting & Nonferrous Alloys, 2013,33(3):204-208.
[1]王怀国,毛萍莉.挤压态AM30镁合金高速冲击载荷下的断裂形貌分析[J].特种铸造及有色合金,2013,33(03):204-208. DOI： 10.15980/j.tzzz.2013.03.012.

Wang Huaiguo1, Mao Pingli2. Failure Mode and Fracture Morphology Analysis of Extruded AM30 Magnesium Alloy under High Strain Rate Loading[J]. Special Casting & Nonferrous Alloys, 2013,33(3):204-208. DOI： 10.15980/j.tzzz.2013.03.012.

摘要

采用扫描电镜（SEM）及光学金相显微镜观察了挤压态AM30镁合金在高应变速率的压缩及拉伸载荷作用下

沿挤压方向及横向断裂之后的微观组织形貌

研究了不同微观形貌的形成原因。结果表明

挤压态AM30镁合金在高速压缩时为脆性断裂

而在高速拉伸时不论是横向还是挤压方向均为韧、脆混合断裂

且随着应变速率的增加脆性增大。除了断裂之外

挤压态AM30镁合金在高速冲击载荷作用下的失效形式还有绝热剪切及内部裂纹扩展。

Abstract

The micro-fracture morphology of the alloy under high strain rate tension and compression loading were observed by scanning electron microscopy（SEM） and optical microscopy（OM）.The tension and compression were conducted along extrusion direction and transverse direction

respectively.The results show that the compression fracture is characterized by brittle mode

while the high strain rate tension fracture is characterized by mixed mode of ductile and brittle.With increasing in the strain rate

the fracture tendecy of brittle to ductility is increased.Besides the fracture

the failure modes of extruded AM30 magnesium alloy under high strain rate belong to adiabatic shear band and crack propagation.

关键词

镁合金高速拉伸高速压缩断口形貌

Keywords

Magnesium AlloyHigh Strain Rate TensionHigh Strain Rate CompressionFracture Morphology