氩气处理对AZ91镁合金高温力学性能的影响

赵正任; 贾征; 王彤; 高源; 郭锦鹏; 胡天润; 柳鑫

doi:10.15980/j.tzzz.2020.04.022

轻有色合金 | 浏览量 : 0 下载量: 66 CSCD: 0

导出
分享
收藏
专辑

氩气处理对AZ91镁合金高温力学性能的影响
Effects of Ar Dehydrogenation on Mechanical Properties of AZ91 Alloy at High Temperature
2020年40卷第4期页码：445-448
纸质出版日期： 2020 ，
DOI： 10.15980/j.tzzz.2020.04.022

扫描看全文

[1]赵正任,贾征,王彤,高源,郭锦鹏,胡天润,柳鑫.氩气处理对AZ91镁合金高温力学性能的影响[J].特种铸造及有色合金,2020,40(04):445-448.

Zhao Zhengren, Jia Zheng, Wang Tong, et al. Effects of Ar Dehydrogenation on Mechanical Properties of AZ91 Alloy at High Temperature[J]. Special Casting & Nonferrous Alloys, 2020,40(4):445-448.
[1]赵正任,贾征,王彤,高源,郭锦鹏,胡天润,柳鑫.氩气处理对AZ91镁合金高温力学性能的影响[J].特种铸造及有色合金,2020,40(04):445-448. DOI： 10.15980/j.tzzz.2020.04.022.

Zhao Zhengren, Jia Zheng, Wang Tong, et al. Effects of Ar Dehydrogenation on Mechanical Properties of AZ91 Alloy at High Temperature[J]. Special Casting & Nonferrous Alloys, 2020,40(4):445-448. DOI： 10.15980/j.tzzz.2020.04.022.

摘要

研究了氩气处理对AZ91镁合金高温力学性能的影响。结果表明

经过氩气处理后

每100g熔体中的氢含量从未处理的14.8cm

降低至7.3cm

除气率高达50.7%;在20、100、175、250、325和400℃对合金分别进行拉伸试验

发现除气对合金抗拉强度和屈服强度的影响随温度升高而逐渐减小

但对伸长率的影响正好相反。在温度低于250℃时除气

合金强度显著提高

伸长率变化不明显

除气对在高温（250～325℃）拉伸时强度影响不大

但明显提高了镁合金的伸长率

另外

应变硬化指数（n）值相差不大（分别为0.04和0.03）。

Abstract

Effects of Ar dehydrogenation on mechanical properties of AZ91 alloy at high temperature were investigated.The results indicate that the hydrogen content can be reduced from 14.8 cm

/100 g to 7.3 cm

/100 g and the degassing efficiency reaches to 50.7%.The effects of degassing on tensile and yield strength of the alloy are decreased with the increase in temperature in AZ91 alloy at 20

100

175

250

325 and 400 ℃

respectively

while that on elongation is opposite to that on strength.The strength of AZ91 alloy after degassing is improved obviously when the temperature is lower than 250 ℃ with little difference on elongation.Degassing has little effect on strength of alloy at the temperature from 250℃to 325℃.However

the elongation of alloy is improved obviously and the strain hardening exponents are basically the same（0.04 and 0.03

respectively）.