    • 高温长时间保温对共晶铝硅合金组织及力学性能的影响

    • Effects of High Temperature and Long Time Holding Temperature on Microstructure and Mechanical Properties of Eutectic Al-Si Alloy

    • 程峰

      123 ，

      程和法

      123 ，

      黄笑梅

      123 ，

      夏明旷

      123 ，

      朱启明

      123
    • 2019年39卷第8期 页码：918-921   

      纸质出版日期： 2019 ，

    • DOI： 10.15980/j.tzzz.2019.08.027     

    扫 描 看 全 文

  • 引用

  • [1]程峰,程和法,黄笑梅,夏明旷,朱启明.高温长时间保温对共晶铝硅合金组织及力学性能的影响[J].特种铸造及有色合金,2019,39(08):918-921. DOI： 10.15980/j.tzzz.2019.08.027.
    Cheng Feng, Cheng Hefa, Huang Xiaomei, et al. Effects of High Temperature and Long Time Holding Temperature on Microstructure and Mechanical Properties of Eutectic Al-Si Alloy[J]. Special Casting & Nonferrous Alloys, 2019,39(8):918-921. DOI： 10.15980/j.tzzz.2019.08.027.
  •  
  •  

  • HTML全文

  • 参考文献

  • 出版信息

  • 数据统计

论文导航

摘要

对经过变质和T6处理的Al-12Si-3.5Cu-1Mg-2Ni合金在300℃下进行25～400h的长时间保温,研究其在高温长时间保温下组织和性能的演变。结果表明,在300℃下保温25～100h后,共晶Si形态由颗粒状变成棒状,晶粒尺寸增大,数量减少,出现了粗大块状Si相;保温200～400h后,粗大块状Si相尺寸减小,共晶Si形态由棒状又变成了颗粒状,尺寸减小,数量增加。合金化合物相一直析出聚集增长,形成了针状Al-Ni-Cu或者Al-Cu-Ni相。合金的力学性能下降,抗拉强度从332.34MPa下降到185.65MPa,伸长率先下降后上升。

译

Abstract

Al-12Si-3.5Cu-1.0Mg-2.0Ni alloys with modification and T6 treatment were conducted at 300 ℃ for 25～400 h.The evolution of microstructure and properties of alloy under high temperature and long time holding temperature was analyzed.The results show that the eutectic Si morphology is changed from granular to rod-like at 300℃ for 25～100 h,and grain size is increased with number decreases,and the coarse bulk Si phase appears.After 200～400 h,the size of the coarse bulk Si phase is decreased,and the eutectic Si morphology is changed from rod-like to granular,meanwhile,the size is decreased with the quantity increases.The precipitation,aggregation and growth of alloying compounds form acicular Al-Ni-Cu or Al-Cu-Ni phases.The mechanical properties of the alloy are decreased,where the tensile strength is decreased from 332.34 MPa to 185.65 MPa,and the elongation is decreased firstly and then increased.

译

关键词

热处理; 长时间; 微观组织; 力学性能

译

Keywords

Heat Treatment; Long Time; Microstructure; Mechanical Properties

译

文章被引用时，请邮件提醒。
提交

相关文章

相关作者

杨湘杰 南昌大学先进制造学院;江西省高性能精确成形重点实验室
宫梦奇 南昌大学先进制造学院;江西省高性能精确成形重点实验室
白娜 桂林电子科技大学
邹伟峰 南昌大学先进制造学院;江西省高性能精确成形重点实验室
郑彬 南昌大学先进制造学院;江西省高性能精确成形重点实验室
刘钦标 南昌大学先进制造学院;江西省高性能精确成形重点实验室
户凤荣 吉林化工学院航空工程职业技术学院
余国康 上海航天精密机械研究所; 哈尔滨工业大学材料科学与工程学院

相关机构

南昌大学先进制造学院
江西省高性能精确成形重点实验室
桂林电子科技大学
吉林化工学院航空工程职业技术学院
上海航天精密机械研究所
0