原位自生Fe<sub>3</sub>Al增强Cu基复合材料的组织和性能

张玉伟; 康慧君; 张邵建; 王同敏

doi:10.15980/j.tzzz.2019.07.020

复合材料 | 浏览量 : 0 下载量: 84 CSCD: 0

导出
分享
收藏
专辑

原位自生Fe₃Al增强Cu基复合材料的组织和性能
Microstructure and Mechanical Properties of Fe₃Al Reinforced Copper Matrix Composites Prepared by In-situ Reaction
2019年39卷第7期页码：776-780
纸质出版日期： 2019 ，
DOI： 10.15980/j.tzzz.2019.07.020

扫描看全文

[1]张玉伟,康慧君,张邵建,王同敏.原位自生Fe_3Al增强Cu基复合材料的组织和性能[J].特种铸造及有色合金,2019,39(07):776-780.

Zhang Yuwei, Kang Huijun, Zhang Shaojian, et al. Microstructure and Mechanical Properties of Fe₃Al Reinforced Copper Matrix Composites Prepared by In-situ Reaction[J]. Special Casting & Nonferrous Alloys, 2019,39(7):776-780.
[1]张玉伟,康慧君,张邵建,王同敏.原位自生Fe_3Al增强Cu基复合材料的组织和性能[J].特种铸造及有色合金,2019,39(07):776-780. DOI： 10.15980/j.tzzz.2019.07.020.

Zhang Yuwei, Kang Huijun, Zhang Shaojian, et al. Microstructure and Mechanical Properties of Fe₃Al Reinforced Copper Matrix Composites Prepared by In-situ Reaction[J]. Special Casting & Nonferrous Alloys, 2019,39(7):776-780. DOI： 10.15980/j.tzzz.2019.07.020.

摘要

通过XRD、OM、SEM、TEM和拉伸试验等手段

研究了不同Fe

Al含量和变形工艺对原位自生Fe

Al增强Cu基复合材料显微组织和力学性能的影响。结果表明

当Fe

Al含量增加时

复合材料晶粒明显细化;第二相以纳米尺度的Fe

Al为主

且均匀分布在Cu基体中;经过冷轧和退火处理后

晶粒进一步细化

同时强度得到提升。Fe和Al含量分别为10%的复合材料在经过90%冷轧变形和350℃×1h退火处理后

显微硬度（HV）和抗拉强度分别达到272和871MPa。

Abstract

The effects of Fe

Al reinforced particles and deformation technology on microstructures and mechanical properties of the Fe

Al/Cu composites fabricated by in-situ reaction were investigated by XRD

SEM

TEM and tensile testing.The results show that with the increase of Fe

Al contents

the grain size is decreased.The nanoscale Fe

Al particles are uniformly distributed in Cu matrix.After cold rolling and annealing

obvious grain refinement and significant increment in strength are observed.After 90%cold-rolling reduction

the hardness and strength of 10% Fe

Al/Cu composite containing 10% Fe and Al elements reach 272 HV and 871 MPa

respectively.

关键词

复合材料Fe3Al第二相原位自生法力学性能

Keywords

CompositesFe3Al Second PhaseIn-situ ReactionMechanical Properties

references

文章被引用时，请邮件提醒。

提交

喷射沉积SiC_P/FVS0612薄板微观组织及力学性能

铝含量对碳纳米管/镁基复合材料的影响

热加工工艺对喷射沉积SiC_p/Al-Fe-V-Si组织与性能的影响

多次循环塑性变形对Mg₂Si/Mg-5Zn-2.5Er复合材料组织与性能的影响

SiC_p/Al复合材料等径角挤压工艺研究

原位自生Fe3Al增强Cu基复合材料的组织和性能

Microstructure and Mechanical Properties of Fe3Al Reinforced Copper Matrix Composites Prepared by In-situ Reaction

DOI： 10.15980/j.tzzz.2019.07.020

摘要

Abstract

关键词

Keywords

references

原位自生Fe₃Al增强Cu基复合材料的组织和性能

Microstructure and Mechanical Properties of Fe₃Al Reinforced Copper Matrix Composites Prepared by In-situ Reaction