IC10合金定向空心叶片“黑线”缺陷鉴别与原因分析

王祯; 杨泽南; 于俊杰; 张强; 杨志刚

doi:10.15980/j.tzzz.2019.07.016

精密铸造 | 浏览量 : 0 下载量: 51 CSCD: 0

导出
分享
收藏
专辑

IC10合金定向空心叶片“黑线”缺陷鉴别与原因分析
Characterization Method of Defects in Superalloy IC10 during Directionally Solidification and Analysis of Defects′ Formation Mechanism
2019年39卷第7期页码：756-760
纸质出版日期： 2019 ，
DOI： 10.15980/j.tzzz.2019.07.016

扫描看全文

[1]王祯,杨泽南,于俊杰,张强,杨志刚.IC10合金定向空心叶片“黑线”缺陷鉴别与原因分析[J].特种铸造及有色合金,2019,39(07):756-760.

Wang Zhen, Yang Ze′nan, Yu Junjie, et al. Characterization Method of Defects in Superalloy IC10 during Directionally Solidification and Analysis of Defects′ Formation Mechanism[J]. Special Casting & Nonferrous Alloys, 2019,39(7):756-760.
[1]王祯,杨泽南,于俊杰,张强,杨志刚.IC10合金定向空心叶片“黑线”缺陷鉴别与原因分析[J].特种铸造及有色合金,2019,39(07):756-760. DOI： 10.15980/j.tzzz.2019.07.016.

Wang Zhen, Yang Ze′nan, Yu Junjie, et al. Characterization Method of Defects in Superalloy IC10 during Directionally Solidification and Analysis of Defects′ Formation Mechanism[J]. Special Casting & Nonferrous Alloys, 2019,39(7):756-760. DOI： 10.15980/j.tzzz.2019.07.016.

摘要

以IC10合金定向空心叶片为研究对象

确认其铸造缺陷的位置分布及宏观形貌

并对缺陷的形貌特征及产生原因进行分析

认为这主要与凝固后期补缩不足有关。对铸件的局部化学成分进行分析

讨论Al、Hf等合金元素对补缩过程热力学与动力学的影响。最后

采用相场模拟法探究了局部散热情况对IC10合金凝固过程的影响。结果表明

当铸件以较低的冷却速率冷却时

易在枝晶间形成连通的液相通道

与显微组织观察中的缺陷形貌一致。

Abstract

The casting defect distribution and macro-morphology of the directionally solidified IC10 superalloy turbine blades were described.In addition

the microscopic morphology and the formation mechanism of defects were analyzed

which could be related with the inadequate feeding during the last stage of solidification.Afterwards

the chemical composition in the vicinity of defect region was analyzed in order to understand the effect of Al

Hf on the thermodynamic and kinetic of feeding process.Finally

phase field simulation via MICRess software was carried out to predict the effectiveness of heat radiation on the solidification process at various cooling rate.The results reveal that with cooled at a lower rate

untransformed liquid tends to form connected channels in interdendritic region

which is in accordance with the morphology of defects observed experimentally.