玻璃固化用电磁冷坩埚温度场研究
Temperature Field during Melting and Solidification of Glass with Electromagnetic Cold Crucible
2017年37卷第11期页码：1196-1200
纸质出版日期： 2017 ，
DOI： 10.15980/j.tzzz.2017.11.010

扫描看全文

[1]明玉周,李铮,曹德伟,杨耀华,王瑞,陈瑞润,郭景杰.玻璃固化用电磁冷坩埚温度场研究[J].特种铸造及有色合金,2017,37(11):1196-1200.

Ming Yuzhou, Li Zheng, Cao Dewei, et al. Temperature Field during Melting and Solidification of Glass with Electromagnetic Cold Crucible[J]. Special Casting & Nonferrous Alloys, 2017,37(11):1196-1200.
[1]明玉周,李铮,曹德伟,杨耀华,王瑞,陈瑞润,郭景杰.玻璃固化用电磁冷坩埚温度场研究[J].特种铸造及有色合金,2017,37(11):1196-1200. DOI： 10.15980/j.tzzz.2017.11.010.

Ming Yuzhou, Li Zheng, Cao Dewei, et al. Temperature Field during Melting and Solidification of Glass with Electromagnetic Cold Crucible[J]. Special Casting & Nonferrous Alloys, 2017,37(11):1196-1200. DOI： 10.15980/j.tzzz.2017.11.010.

摘要

使用冷坩埚对核废料进行固化处理后将固化体深埋可以防止核废料污染环境

而固化时熔体的温度分布将直接影响固化体的质量。利用Ansys软件建立了温度场计算模型

并通过试验验证了模型的准确性。利用此模型分析了冷坩埚玻璃固化时熔体不同位置以及不同电源参数条件下的温度分布。结果表明

随着电流值和频率的增加

加热到工作温度的时间缩短

但温度梯度增大

使熔体内部温度分布不均匀。熔炼过程中应根据实际情况添加机械搅拌。

Abstract

Through using cold crucible to curing nuclear waste and deeply burying solidified body

the detriment of nuclear waste for environment could be prevented.The temperature distribution of melt interior will impact the quality of the solidified body directly.A temperature field calculation model was established by Ansys software.Then accuracy of the model was verified by experiments.The distribution of temperature field in melt was simulated and the distribution of temperature was analyzed at different power parameters by using the model.The results reveal that with the increase of current value and frequency

heating time to the operating temperature can be shortened

however

the temperature gradient can be enlarged

which cause the uneven distribution in melt.Smelting process should set mechanical agitation on the basis of physical conditions.