    • 坩埚半径对电磁搅拌制备半固态A356浆料电磁场分布的影响

    • Effects of Crucible Radius on Electromagnetic Field Distribution during Fabrication of Electric-stirring Semi-solid A356 Aluminum Alloy Slurry

    • 陈志平

      1

      刘政

      1

      陈涛

      2
    • 2017年37卷第9期 页码:961-965   

      纸质出版日期: 2017

    • DOI: 10.15980/j.tzzz.2017.09.009     

    扫 描 看 全 文

  • 引用

  • [1]陈志平,刘政,陈涛.坩埚半径对电磁搅拌制备半固态A356浆料电磁场分布的影响[J].特种铸造及有色合金,2017,37(09):961-965. DOI: 10.15980/j.tzzz.2017.09.009.
    Chen Zhiping, Liu Zheng, Chen Tao. Effects of Crucible Radius on Electromagnetic Field Distribution during Fabrication of Electric-stirring Semi-solid A356 Aluminum Alloy Slurry[J]. Special Casting & Nonferrous Alloys, 2017,37(9):961-965. DOI: 10.15980/j.tzzz.2017.09.009.
  •  
  •  
    论文导航

    摘要

    提出了坩埚半径的设计思路,研究了坩埚半径对电磁搅拌制备半固态A356铝合金浆料时磁感应强度和电磁力分布的影响。通过ANSYS 15.0模拟了不同坩埚半径中半固态A356铝合金浆料受到的磁感应强度和电磁力沿坩埚径向的变化趋势。模拟结果表明,磁感应强度从坩埚中心沿坩埚径向0.85倍距离左右逐渐增大;电磁力整体上随坩埚半径的增大而增大,且增加的幅度越来越大,电磁力从坩埚中心到坩埚径向上0.9倍距离左右逐渐增大,而在边缘处急剧减小。对不同坩埚半径的试验结果进行对比,发现最佳的坩埚半径为30mm。

    Abstract

    The design idea of crucible radius was proposed,and influence of crucible radius on the magnetic flux density and electromagnetic force distribution of semisolid A356 aluminum alloy slurry was investigated.The change of magnetic flux density and electromagnetic force along the radius of the crucible for semisolid A356 aluminum alloy was simualted by ANSYS 15.0.The simulated results show that the magnetic flux intensity is increased from the center to the distance about 0.85 times of the crucible radius,decreased sharply and then increased near the edge.The electromagnetic force is increased with the increase of the crucible radius,and the increment-amplitude is larger and larger.The electromagnetic force is increased from the center to the distance about 0.9times of the crucible radius,decreased sharply at the edge.The experimental results of different crucible radius were compared with the simulated ones.The results reveal that the optimum crucible radius is 30 mm in the preparation of high quality semisolid aluminum alloy slurry.

    关键词

    坩埚半径; ANSYS; 电磁搅拌; 磁感应强度

    Keywords

    Crucible Radius; ANSYS; Electromagnetic Stirring; Magnetic Flux Density

    文章被引用时,请邮件提醒。
    提交

    相关作者

    魏亚芳 东北大学材料电磁过程研究教育部重点实验室;东北大学冶金学院
    邓安元 东北大学材料电磁过程研究教育部重点实验室;东北大学冶金学院
    王恩刚 东北大学材料电磁过程研究教育部重点实验室;东北大学冶金学院
    张景新   北京有色金属研究总院  ;  东风汽车公司  
    张奎   北京有色金属研究总院  ;  东风汽车公司  
    杜东朝   北京有色金属研究总院  ;  东风汽车公司  
    徐骏   北京有色金属研究总院  ;  东风汽车公司  
    石力开   北京有色金属研究总院  ;  东风汽车公司  

    相关机构

    东北大学材料电磁过程研究教育部重点实验室
    东北大学冶金学院
      北京有色金属研究总院  
      东风汽车公司  
      北京科技大学  
    0