自孕育法制备ZA27合金半固态浆料水淬组织
Microstructure of ZA27 Alloy Water-quenched Semi-solid Slurry Prepared by Self-inoculation Method
2016年36卷第3期页码：252-255
纸质出版日期： 2016 ，
DOI： 10.15980/j.tzzz.2016.03.008

扫描看全文

[1]邱谨,李元东,李明,张继渊,郑宏强.自孕育法制备ZA27合金半固态浆料水淬组织[J].特种铸造及有色合金,2016,36(03):252-255.

Qiu jin, Li Yuandong, Li Ming, et al. Microstructure of ZA27 Alloy Water-quenched Semi-solid Slurry Prepared by Self-inoculation Method[J]. Special Casting & Nonferrous Alloys, 2016,36(3):252-255.
[1]邱谨,李元东,李明,张继渊,郑宏强.自孕育法制备ZA27合金半固态浆料水淬组织[J].特种铸造及有色合金,2016,36(03):252-255. DOI： 10.15980/j.tzzz.2016.03.008.

Qiu jin, Li Yuandong, Li Ming, et al. Microstructure of ZA27 Alloy Water-quenched Semi-solid Slurry Prepared by Self-inoculation Method[J]. Special Casting & Nonferrous Alloys, 2016,36(3):252-255. DOI： 10.15980/j.tzzz.2016.03.008.

摘要

采用自孕育法制备了ZA27合金半固态浆料

研究了不同熔体处理温度、等温保温温度和等温保温时间对ZA27合金半固态浆料水淬组织的影响。结果表明

自孕育法制备半固态浆料

其形核包括两个阶段

能够有效细化ZA27合金的晶粒

获得细小的蔷薇状等轴晶。在等温保温球化过程中

随等温保温时间的延长

平均晶粒尺寸不断增加

形状因子先减小后增大。适合ZA27合金半固态浆料的等温保温温度为470℃

等温保温时间为3min

平均晶粒尺寸为60.02μm。

Abstract

The semi-solid slurry of ZA27 casting alloy was prepared by self-inoculation method.Waterquenched microstructure of ZA27semi-solid slurry at different treatment temperature

isothermal holding temperature and holding time was observed.The results indicate that the self-inoculation method with two inoculation stages can refine effectively ZA27 melt to achieve fine rosette equaixed grain.During isothermal holding process

average grain size of the ZA27 alloy slurry is increased with isothermal holding time increase

while grain shape factor is increased firstly and then decreased.With isothermal holding temperature of 470℃and isothermal holding time of 3min

the corresponding average grain size is 60.02μm.

关键词

自孕育法水淬组织形核等温保温

Keywords

Self-inoculation MethodWater-quenched MicrostructureNucleationIsothermal Holding

references

文章被引用时，请邮件提醒。

提交

半固态ZL101合金初生相在固液区间等温保温时形貌演变

金属凝固微观组织形成的数值模拟

导流器在AZ91D镁合金半固态组织形成中的作用

Cu_44.25Ag_14.75Zr₃₆Ti₅非晶合金的晶化行为

金属型铸造与半固态流变压铸2024铝合金组织对比