锂对ZA27合金高温力学性能的影响

苏德煌

浏览量 : 0 下载量: 61 CSCD: 32

导出
分享
收藏
专辑

锂对ZA27合金高温力学性能的影响
Effect of Li on Mechanical Properties at High Temperature for ZA27 Alloy
1998年第6期
纸质出版日期： 1998 ，
DOI：

扫描看全文

[1]苏德煌.锂对ZA27合金高温力学性能的影响[J].特种铸造及有色合金,1998(06):28-29.

Su Dehuang. Effect of Li on Mechanical Properties at High Temperature for ZA27 Alloy[J]. Special Casting & Nonferrous Alloys, 1998,(6).
[1]苏德煌.锂对ZA27合金高温力学性能的影响[J].特种铸造及有色合金,1998(06):28-29. DOI：

Su Dehuang. Effect of Li on Mechanical Properties at High Temperature for ZA27 Alloy[J]. Special Casting & Nonferrous Alloys, 1998,(6). DOI：

摘要

研究了锂对ＺＡ２７合金高温拉伸性能的影响。结果表明，添加适量的锂后，合金的组织明显细化，晶界相变为细碎且分布不连续，从而显著提高了合金的高温强度。用锂强化的合金１５０℃和１８０℃时的抗拉强度分别为２３０ＭＰａ和１８５ＭＰａ，分别比ＺＡ２７合金提高４１．１％和４２．３％。

Abstract

The influence of Li on the tensile properties of ZA27 alloy at high temperature has been investigated. The results show that the microstructure of the alloy is significantly refined and crystals at grain boundaries are broken and distributed discontinuously after an appropriate Li addition. As a result

the tensile strength at high temperature significantly increases. The tensile strength of the Li strengthened alloy reaches 230 MPa and 185 MPa and increases by 41.1% and 42.3% more than that of conventional ZA27 alloy respectively.