锡青铜叶轮的铸造缺陷分析和改进措施
Analysis of Defects and Prevention Measures of Bronze Impeller
2005年第3期页码：191-192
纸质出版日期： 2005 ，
DOI：

扫描看全文

[1]邹日荣.锡青铜叶轮的铸造缺陷分析和改进措施[J].特种铸造及有色合金,2005(03):191-192+128.

Zou Rirong. Analysis of Defects and Prevention Measures of Bronze Impeller[J]. Special Casting & Nonferrous Alloys, 2005,(3):191-192.
[1]邹日荣.锡青铜叶轮的铸造缺陷分析和改进措施[J].特种铸造及有色合金,2005(03):191-192+128. DOI：

Zou Rirong. Analysis of Defects and Prevention Measures of Bronze Impeller[J]. Special Casting & Nonferrous Alloys, 2005,(3):191-192. DOI：

摘要

分析了锡青铜叶轮铸件出现的缩孔、气孔、冲砂等缺陷的原因。采取改用冷硬树脂砂造型、安放冷铁和搞好生产过程的质量控制等措施

基本上消除了这些缺陷

获得了质量稳定的合格铸件。

Abstract

The reasons resulting in the shrinkage porosity

gas-hole and impacted sand in bronze castings were analyzed.These defects were eliminated and the sound castings with steady quality were obtained by adopting cooling-hardness resin sand and setting chilled iron as well as controlling the production process.