Gd对Mg-2Al-Zn合金微观组织及力学性能的影响
Effects of Gd Addition on Microstructure and Mechanical Properties of Mg-2Al-Zn Alloy
2007年第8期页码：642-644
纸质出版日期： 2007 ，
DOI：

扫描看全文

[1]靳广永,吴玉峰,李建辉,杜文博.Gd对Mg-2Al-Zn合金微观组织及力学性能的影响[J].特种铸造及有色合金,2007(08):642-644+573-574.

Jin Guangyong, Wu Yufeng, Li Jianhui, et al. Effects of Gd Addition on Microstructure and Mechanical Properties of Mg-2Al-Zn Alloy[J]. Special Casting & Nonferrous Alloys, 2007,(8):642-644.
[1]靳广永,吴玉峰,李建辉,杜文博.Gd对Mg-2Al-Zn合金微观组织及力学性能的影响[J].特种铸造及有色合金,2007(08):642-644+573-574. DOI：

Jin Guangyong, Wu Yufeng, Li Jianhui, et al. Effects of Gd Addition on Microstructure and Mechanical Properties of Mg-2Al-Zn Alloy[J]. Special Casting & Nonferrous Alloys, 2007,(8):642-644. DOI：

摘要

研究了稀土Gd的添加对铸态Mg-2Al-Zn合金显微组织和力学性能的影响。结果表明

Mg-2Al-Zn-xGd合金由α-Mg和Al2Gd两相组成

Al优先与Gd反应生成Al2Gd

且合金中Al2Gd的数量和形态受Gd的添加量影响。弥散分布的Al2Gd使合金室温力学性能得到显著提高

在Gd的添加量（质量分数）为2%时

抗拉强度和屈服强度分别达到252MPa和135MPa。但Gd的添加量达到3%时

Al2Gd相尺寸变大、数量过多

导致合金的力学性能迅速下降。颗粒状和针状Al2Gd在晶界上或基体上的团聚导致合金由韧性断裂转变为解理断裂。

Abstract

Effects of Gd addition on the microstructure and mechanical properties of Mg-2Al-Zn magnesium alloy were investigated. The results reveal that the microstructure of as-cast Mg-2Al-Zn-xGd alloy is composed of α-Mg and Al2Gd phase formed by the prior reaction of Al and Gd. The amounts and morphology of Al2Gd phase are controlled by the Gd addition. Meanwhile

the dispersive Al2Gd phase had a positive contribution to greatly improve the mechanical properties of the alloy. The tensile strength and yield strength of the alloy are 252 MPa and 135 MPa respectively with 2% Gd addition

while the mechanical properties of the alloy can be obviously deteriorated as a result of the increase of the amount and size of Al2Gd phase with 3% Gd addition. The segregation of polygon and acicular Al2Gd particles in the boundary or the matrix can result in the change of fracture morphology from ductility fracture into cleavage fracture.