拉伸复合法制备Cu-Al复合接触线

复合材料 | 浏览量 : 0 下载量: 141 CSCD: 3

扫描看全文

[1]杨斌,张迎晖,李明茂,赵鸿金,周火清.拉伸复合法制备Cu-Al复合接触线[J].特种铸造及有色合金,2008(11):875-876+818.

Yang Bin1, Zhang Yinghui1, Li Mingmao1, et al. Preparation of Cu Cladding Al Contact Wire by Drawing Compound Method[J]. Special Casting & Nonferrous Alloys, 2008,(11):875-876.
[1]杨斌,张迎晖,李明茂,赵鸿金,周火清.拉伸复合法制备Cu-Al复合接触线[J].特种铸造及有色合金,2008(11):875-876+818. DOI：

Yang Bin1, Zhang Yinghui1, Li Mingmao1, et al. Preparation of Cu Cladding Al Contact Wire by Drawing Compound Method[J]. Special Casting & Nonferrous Alloys, 2008,(11):875-876. DOI：

采用拉伸复合法制备了截面积为160mm2

线密度为（1.0±0.1）kg/m的Cu-Al复合接触线。性能检测结果表明

铜铝复合接触线的综合电导率为45.82MS/m

结合力达到60N/mm

拉断力为47kN

可用作载流量为2000A的磁浮动力轨。

Cu cladding Al contact wire with 160mm2 in cross section and（1.0±0.1） kg/m in linear density was fabricated by the drawing compound method

and properties of the wire were examined.It is found that the comprehensive electronic conductivity

bonding force and fracture force of the Cu cladding Al contact wire make 45.82 MS/m

60N/m and 47kN

respectively

which can be used for magnetic floating power track with loads of 2000A.

拉伸复合铜铝复合接触线

Drawing Compound MethodCu Cladding AlContact Wire