V-5Cr-5Ti alloy was prepared by double vacuum arc remelting（VAR） and then forging as well as warm rolling and annealing treatment to realize desirable chemical composition and mechanical properties

and properties and microstructure of the prepared alloy were characterized by chemical analysis

OM（optical microscope）

SEM（scanning electron microscope） and tensile testing.The results show that oxygen content in the alloy can be controlled in 500

6

00 μg/g after double arc remelting

however

grain exhibits coarse in the ingot.Fine equiaxed grain with size lower than 100 μm can be observed in the prepared alloy with forging at 1 150 ℃ and warm rolling at 450 ℃ and then annealing at 1000 ℃ for one hour

and yield strength

tensile strength

elongation and area reduction reach 356 MPa

449 MPa

31.5% and 71.5%

respectively.