Effects of Pulsed Magnetic Field on Microstructure and Properties of Mg-6Zn-0.5Zr-1Gd Alloy

Mao Xuncong; Chen Leping; Peng Cong; Wei Chenyang; Xin Zhouyuan

doi:10.15980/j.tzzz.2022.07.022

Views : 0 下载量: 54 CSCD: 0

PDF
Export
Share
Collection
Album

Effects of Pulsed Magnetic Field on Microstructure and Properties of Mg-6Zn-0.5Zr-1Gd Alloy
Vol. 42, Issue 7, Pages: 898-903(2022)
Published： 2022 ，
DOI： 10.15980/j.tzzz.2022.07.022

扫描看全文

Mao Xuncong, Chen Leping, Peng Cong, et al. Effects of Pulsed Magnetic Field on Microstructure and Properties of Mg-6Zn-0.5Zr-1Gd Alloy. [J]. Special Casting & Nonferrous Alloys 42(7):898-903(2022)
DOI：

Mao Xuncong, Chen Leping, Peng Cong, et al. Effects of Pulsed Magnetic Field on Microstructure and Properties of Mg-6Zn-0.5Zr-1Gd Alloy. [J]. Special Casting & Nonferrous Alloys 42(7):898-903(2022) DOI： 10.15980/j.tzzz.2022.07.022.

摘要

研究了不同的脉冲磁场参数对Mg-6Zn-0.5Zr-1Gd合金凝固组织及力学性能的影响。结果表明，经脉冲磁场处理后，合金的凝固组织和力学性能明显改善。脉冲电压在0～300 V或模具预热温度在200～600℃内，随着脉冲电压或模具温度增加，其晶粒尺寸均逐渐减小；脉冲频率在0～10 Hz范围内，随着脉冲频率增加，其晶粒尺寸先减小后增大。当脉冲电压为300 V

脉冲磁场为5 Hz

模具预热温度为600℃时，合金的力学性能最优，其抗压强度为271.35 MPa

压缩率为22.5%。与未经过磁场处理的合金相比，抗压强度和压缩率分别提高了28.4%和14.2%。

Abstract

The effects of different pulsed magnetic field parameters on the solidification microstructure and mechanical properties of Mg-Zn-Zr-Gd alloy were investigated.The results reveal that the solidification microstructure and mechanical properties of the alloy are obviously improved under the condition of pulsed magnetic field. With the increase of pulsed voltage（0～300 V） or mould preheating temperature（200～600 ℃）

the grain size in the alloy is decreased gradually. With the increase of pulsed frequency（0～10 Hz）

the grain size of the alloy is decreased firstly and then increased. With the pulsed voltage of 300 V

the pulsed frequency of 5 Hz and the mould preheating temperature of 600 ℃

the mechanical properties of the alloy present desirable

where the compressive strength and the compression rate of the alloy reach 271.35 MPa and 22.5%

resepctively. Compared with those of the alloy without pulsed magnetic field treatment

the compressive strength and compression rate of treated alloy are increased by 28.4% and 14.2%

respectively.

关键词

脉冲磁场Mg-Zn-Zr-Gd合金凝固组织力学性能

Keywords

Pulsed Magnetic FieldMg-Zn-Zr-Gd AlloysSolidification MicrostructureMechanical Properties

references

Alert me when the article has been cited

提交

Effects of the Remelting Treatment on the Solidification Microstructure and Mechanical Properties of the In-situ Synthesized Composites in A356-ZrOCl₂ System

Effect of Pulsed Magnetic Field on Solidified Structure and Mechanical Properties of H62 Brass

Effects of Low Voltage Pulsed Magnetic Field（LVPMF）on Microstructure and Mechanical Properties of Al-12.4Si Alloy

Microstructure and Mechanical Properties of In-situ Mg₂Si/Mg-7Al Composites under a Pulsed Magnetic Field

Effects of Pulsed Magnetic Field on Microstructure and Mechanical Properties of Mg-Zn-Y Alloy