Effects of Al Content on Microstructure and Resistivity of Ti-Al Alloys Prepared by MA-SPS

Xu Can; Chen Zhe; Chen Jingfan; Cai Qizhou

doi:10.15980/j.tzzz.2022.02.011

Views : 0 下载量: 43 CSCD: 0

PDF
Export
Share
Collection
Album

Effects of Al Content on Microstructure and Resistivity of Ti-Al Alloys Prepared by MA-SPS
Vol. 42, Issue 2, Pages: 184-189(2022)
Published： 2022 ，
DOI： 10.15980/j.tzzz.2022.02.011

扫描看全文

Xu Can, Chen Zhe, Chen Jingfan, et al. Effects of Al Content on Microstructure and Resistivity of Ti-Al Alloys Prepared by MA-SPS. [J]. Special Casting & Nonferrous Alloys 42(2):184-189(2022)
DOI：

Xu Can, Chen Zhe, Chen Jingfan, et al. Effects of Al Content on Microstructure and Resistivity of Ti-Al Alloys Prepared by MA-SPS. [J]. Special Casting & Nonferrous Alloys 42(2):184-189(2022) DOI： 10.15980/j.tzzz.2022.02.011.

摘要

采用机械合金化-放电等离子烧结（MA-SPS）技术制备了不同Al含量的Ti-Al合金，研究了Al含量对Ti-Al复合粉末形貌、Ti-Al合金组织与电阻率的影响。结果表明，高能球磨过程中Ti/Al复合粉末扁平化，Al固溶于Ti中，当Al含量高于9%后，部分Al固溶于Ti

而未固溶的Al破碎为细小颗粒附着于Ti颗粒表面，颗粒表面粗糙度增加，颗粒截面呈层状结构。当Al含量为6%时，球磨粉末烧结试样组织为单相α-Ti（Al）固溶体，Al含量为9%～12%

组织为α-Ti（Al）相及其晶界析出的细小α

颗粒。当Al含量超过12%后，组织为α-Ti（Al）固溶体和α

-Ti

Al双相组织。合金电阻率随着Al含量的增加先增大后减小，Al含量为18%时，又略有增加。Al含量为9%时，电阻率达最大值2.074μΩ·m。

Abstract

Ti-Al alloys with different Al contents were fabricated by mechanical alloying and spark plasma sintering（MA-SPS）. The effects of Al content on the composite powder morphologies

microstructure and electrical resistivity of SPS Ti-Al alloys were investigated. The results indicate that Ti-Al composite powders are flattened during high energy ball milling with Al dissolved into Ti. When the content of Al is higher than 9%

part of Al is dissolved into Ti

while the insoluble Al is broken into fine particles and attached to the surface of Ti particles

resulting in the increase of surface roughness

where the cross section of particles presents a layered structure. When the amount of Al is 6%

the microstructure of SPS specimen prepared by ball milled powders is single-phase α-Ti（Al） solid solution

which becomes α-Ti（Al） phase and fine α

particles precipitated in grain boundary when the amount of Al is 9%～12%. When the amount of Al exceeds 12%

the microstructure is dual-phase composed of α-Ti（Al） and α

-Ti

Al. The electrical resistivity of the alloys is firstly increased and then decreased with the increase of Al content

and slightly increased when the amount of Al reaches 18%.The electrical resistivity reaches the maximum value of 2.074 μΩ·m when the Al content is 9%.