Effects of Sr on Solidified Structure and Mechanical Properties of Mg-Gd-Y-Zr Alloy

Xie Dongyuan; Zhou Quan; Chen Ge; Chen Leping; Li Peng

doi:10.15980/j.tzzz.2021.04.011

Views : 0 下载量: 4 CSCD: 0

PDF
Export
Share
Collection
Album

Effects of Sr on Solidified Structure and Mechanical Properties of Mg-Gd-Y-Zr Alloy
Vol. 41, Issue 4, Pages: 445-449(2021)
Published： 2021 ，
DOI： 10.15980/j.tzzz.2021.04.011

扫描看全文

[1]谢东原,周全,陈舸,陈乐平,李鹏.Sr对Mg-Gd-Y-Zr合金凝固组织和力学性能的影响[J].特种铸造及有色合金,2021,41(04):445-449.

Xie Dongyuan, Zhou Quan, Chen Ge, et al. Effects of Sr on Solidified Structure and Mechanical Properties of Mg-Gd-Y-Zr Alloy. [J]. Special Casting & Nonferrous Alloys 41(4):445-449(2021)
[1]谢东原,周全,陈舸,陈乐平,李鹏.Sr对Mg-Gd-Y-Zr合金凝固组织和力学性能的影响[J].特种铸造及有色合金,2021,41(04):445-449. DOI： 10.15980/j.tzzz.2021.04.011.

Xie Dongyuan, Zhou Quan, Chen Ge, et al. Effects of Sr on Solidified Structure and Mechanical Properties of Mg-Gd-Y-Zr Alloy. [J]. Special Casting & Nonferrous Alloys 41(4):445-449(2021) DOI： 10.15980/j.tzzz.2021.04.011.

摘要

利用OM、SEM、EDS、XRD、ICP-AES及万能拉伸试验机等测试手段

分析了0～0.18%的Sr（质量分数）对Mg-6Gd-3Y-0.6Zr合金凝固组织和力学性能的影响。结果表明

随着Sr添加量提高

合金的晶粒尺寸逐渐减小

由42.5μm细化至21.8μm

第二相数量逐渐增多、尺寸逐渐减小、分布情况逐渐改善

其抗拉强度和伸长率提高

分别由170MPa、7.2%提高至192MPa、12.9%。试验中合金的力学性能主要受其凝固组织的影响

其凝固组织越细小

力学性能越高。

Abstract

The effects of 0～0.18% Sr on the solidification structure and mechanical properties of Mg-6Gd-3Y-0.6Zr alloy were investigated by OM

SEM

EDS

XRD

ICP-AES

universal tensile testing machine and other testing methods.The results show that with the increase of Sr addition

grain size in the alloy is decreased gradually from 42.5μm to 21.8μm.The second phase is increased gradually with the decrease of size gradually

and its distribution is improved gradually.Tensile strength and elongation of the alloy are increased gradually from 170 MPa and 7.2% to 192 MPa and 12.9%

respectively.Under the condition of the given experiment

mechanical properties of the alloy is mainly controlled by solidification structure of the alloy.With decreasing in the solidification structure

the mechanical properties are improved obviously.