3D Numerical Simulation of AZ31 Magnesium Alloy during BP-ECAP Process Based on SPH

Song Tingting; Bo Yanqiang; Niu Xiaofeng; Qiu Yunji; Shen Mengqing

doi:10.15980/j.tzzz.2021.02.019

Views : 0 下载量: 26 CSCD: 0

PDF
Export
Share
Collection
Album

3D Numerical Simulation of AZ31 Magnesium Alloy during BP-ECAP Process Based on SPH
Vol. 41, Issue 2, Pages: 219-222(2021)
Published： 2021 ，
DOI： 10.15980/j.tzzz.2021.02.019

扫描看全文

[1]宋婷婷,薄延强,牛晓峰,邱云基,申梦清.基于SPH法的AZ31镁合金BP-ECAP过程三维数值模拟[J].特种铸造及有色合金,2021,41(02):219-222.

Song Tingting, Bo Yanqiang, Niu Xiaofeng, et al. 3D Numerical Simulation of AZ31 Magnesium Alloy during BP-ECAP Process Based on SPH. [J]. Special Casting & Nonferrous Alloys 41(2):219-222(2021)
[1]宋婷婷,薄延强,牛晓峰,邱云基,申梦清.基于SPH法的AZ31镁合金BP-ECAP过程三维数值模拟[J].特种铸造及有色合金,2021,41(02):219-222. DOI： 10.15980/j.tzzz.2021.02.019.

Song Tingting, Bo Yanqiang, Niu Xiaofeng, et al. 3D Numerical Simulation of AZ31 Magnesium Alloy during BP-ECAP Process Based on SPH. [J]. Special Casting & Nonferrous Alloys 41(2):219-222(2021) DOI： 10.15980/j.tzzz.2021.02.019.

摘要

光滑粒子流体动力学方法（Smooth Particle Hydrodynamics

SPH）在求解大变形问题方面具有优势。基于SPH法编写程序对AZ31镁合金的BP-ECAP过程进行三维数值模拟

并与相关研究文献进行对比

验证了编写的SPH法背压程序的正确性。对不同工艺参数下AZ31镁合金的背压-等通道挤压过程进行模拟

并从等效塑性应变及损伤值分布角度进行分析。模拟结果表明

选择恰当的背压值能有效地阻止镁合金变形过程中裂纹的萌生及扩展。

Abstract

Smooth Particle Hydrodynamics（SPH）is a meshless particle method

which has advantages in solving large deformation problems.A three-dimensional numerical simulation of AZ31 magnesium alloy during BPECAP process was carried out based on the SPH method.The simulated results were consistent with those in the literature

which verified the correctness of the SPH method back pressure program.The back pressure-equal channel extrusion process of AZ31 magnesium alloy under different process parameters were predictively simulated and analyzed from the perspective of equivalent plastic strain and damage value distribution.The simulated results reveal that the appropriate back pressure value can prevent effectively the initiation and propagation of cracks during the deformation of magnesium alloys.