Microstructure and Mechanical Properties of ZM5 Alloy Treated by Two Stage Aging

Feng Yicheng; Wu Yibang; Wang lei; Zhao Sicong; Wang Liping

doi:10.15980/j.tzzz.2021.02.002

Views : 0 下载量: 56 CSCD: 0

PDF
Export
Share
Collection
Album

Microstructure and Mechanical Properties of ZM5 Alloy Treated by Two Stage Aging
Vol. 41, Issue 2, Pages: 138-141(2021)
Published： 2021 ，
DOI： 10.15980/j.tzzz.2021.02.002

扫描看全文

[1]冯义成,吴义邦,王雷,赵思聪,王丽萍.双级时效热处理ZM5合金的显微组织和力学性能[J].特种铸造及有色合金,2021,41(02):138-141.

Feng Yicheng, Wu Yibang, Wang lei, et al. Microstructure and Mechanical Properties of ZM5 Alloy Treated by Two Stage Aging. [J]. Special Casting & Nonferrous Alloys 41(2):138-141(2021)
[1]冯义成,吴义邦,王雷,赵思聪,王丽萍.双级时效热处理ZM5合金的显微组织和力学性能[J].特种铸造及有色合金,2021,41(02):138-141. DOI： 10.15980/j.tzzz.2021.02.002.

Feng Yicheng, Wu Yibang, Wang lei, et al. Microstructure and Mechanical Properties of ZM5 Alloy Treated by Two Stage Aging. [J]. Special Casting & Nonferrous Alloys 41(2):138-141(2021) DOI： 10.15980/j.tzzz.2021.02.002.

摘要

以ZM5合金为研究对象

通过显微组织分析和力学性能测试等手段

研究了其不同状态的显微组织和力学性能。结果表明

铸态ZM5合金中存在呈网状分布的粗大不规则块状β-Mg

相;固溶处理后

β-Mg

相溶入α-Mg基体中

仅有少量残余的AlMn相;经T6处理后

沿晶界析出片层状β-Mg

相;经双级时效处理后

沿晶界析出片层状β-Mg

相及在晶内析出细小的针片状β-Mg

相。与铸态相比

热处理后ZM5合金的抗拉强度大幅提升;经双级时效处理后

其抗拉强度可达285MPa

比T6处理后的抗拉强度高20MPa。

Abstract

The microstructure and mechanical behavior of ZM5 alloy with different conditions were carried out by microstructural analysis and tensile testing.The results reveal that there exist many coarse blocky β-Mg

phase in as-cast ZM5 alloy

which is distributed in form of netlike on the grain boundary.After solution treatment

the β-Mg

phase is dissolved intoα-Mg matrix

and a few Al-Mn phase remains.The lamellar β-Mg

phase is precipitated along the grain boundary in ZM5 alloy after T6 treatment.After two stage aging treatment

the lamellar β-Mg

phase is precipitated along the grain boundary and fine acicular β-Mg

phase is precipitated inside grain.Compared to that of as-cast ZM5 alloy

the ultimate tensile strength of heat treated ZM5 alloy is enhanced greatly.The ultimate tensile strength of ZM5 alloy treated by two stage aging can reach 285 MPa

which is 20 MPa higher than that of ZM5 alloy treated by T6.