Effects of Al-5Ti-1B Refiner on Local Shrinkage in Aluminum Alloy Die Castings
Vol. 40, Issue 11, Pages: 1253-1255(2020)
Published： 2020 ，
DOI： 10.15980/j.tzzz.2020.11.016

扫描看全文

[1]王龙生,孔令东,杨同,曹海旺.Al-5Ti-1B细化剂对铝合金压铸件局部收缩的影响[J].特种铸造及有色合金,2020,40(11):1253-1255.

Wang Longsheng, Kong Lingdong, Yang Tong, et al. Effects of Al-5Ti-1B Refiner on Local Shrinkage in Aluminum Alloy Die Castings. [J]. Special Casting & Nonferrous Alloys 40(11):1253-1255(2020)
[1]王龙生,孔令东,杨同,曹海旺.Al-5Ti-1B细化剂对铝合金压铸件局部收缩的影响[J].特种铸造及有色合金,2020,40(11):1253-1255. DOI： 10.15980/j.tzzz.2020.11.016.

Wang Longsheng, Kong Lingdong, Yang Tong, et al. Effects of Al-5Ti-1B Refiner on Local Shrinkage in Aluminum Alloy Die Castings. [J]. Special Casting & Nonferrous Alloys 40(11):1253-1255(2020) DOI： 10.15980/j.tzzz.2020.11.016.

摘要

针对Al-9Si-3Cu铝合金压铸件的铸造缺陷

采用Al-Ti-B细化剂对铝液进行细化处理。结果发现

未使用Al-5Ti-1B细化剂生产的压铸件

会在其局部厚壁部位产生缩坑、缩裂或者内部出现缩松、缩孔等较明显的铸造缺陷

而使用了Al-5Ti-1B细化剂的铸件

无论外观缩坑、缩裂或者内部缩松、缩孔等缺陷均得到了明显改善。经力学性能测试表明

采用Al-5Ti-1B细化剂处理的铸件

其力学性能明显优于未使用Al-Ti-B细化剂处理的压铸件。

Abstract

Aiming at the casting defects in the die casting aluminum alloy components

the effects of Al-5 Ti-1 B refiner on aluminum melt were analyzed. It is found that shrinkage hole

shrinkage cracks at local wall-thickness or internal casting defects such as shrinkage porosities can be observed in the aluminum alloy die castings without Al-Ti-B refiner modification treatment

while the alloy with Al-5 Ti-1 B refiner modification treatment

the defects in the alloy can be improved greatly. In addition

the mechanical properties of the alloy with Al-5 Ti-1 B refiner modification treatment are superior to those of one without Al-5 Ti-1 B modification treatment.