Effects of Melt Mixing Treatment on the Microstructure of A356 Aluminum Alloy
Vol. 40, Issue 4, Pages: 453-455(2020)
Published： 2020 ，
DOI： 10.15980/j.tzzz.2020.04.024

扫描看全文

[1]孙虎,钟鲁宁,傅小明,张月,纪伟进.熔体混合处理对A356铝合金组织的影响[J].特种铸造及有色合金,2020,40(04):453-455.

Sun Hu, Zhong Luning, Fu Xiaoming, et al. Effects of Melt Mixing Treatment on the Microstructure of A356 Aluminum Alloy. [J]. Special Casting & Nonferrous Alloys 40(4):453-455(2020)
[1]孙虎,钟鲁宁,傅小明,张月,纪伟进.熔体混合处理对A356铝合金组织的影响[J].特种铸造及有色合金,2020,40(04):453-455. DOI： 10.15980/j.tzzz.2020.04.024.

Sun Hu, Zhong Luning, Fu Xiaoming, et al. Effects of Melt Mixing Treatment on the Microstructure of A356 Aluminum Alloy. [J]. Special Casting & Nonferrous Alloys 40(4):453-455(2020) DOI： 10.15980/j.tzzz.2020.04.024.

摘要

采用熔体混合技术处理A356铝合金

并通过再次重熔加热研究熔体混合处理细化效果的稳定性。利用光学显微镜观察合金组织

用Image Pro金相分析软件测定了初生α-Al相的平均直径。结果表明

熔体混合技术能较好地细化A356铝合金中的初生α-Al相

且A356铝合金的熔体混合处理在650℃下具有较好的一次重熔稳定性。

Abstract

The A356 aluminum alloy was treated by melt mixing treatment

and the stability of the melt mixing treatment was analyzed by remelting heating.The microstructure of the A356 alloy was observed with an optical microscope

and the average diameter of the primaryα-Al phase was determined by Image Pro metallographic analysis software.The results show that the melt mixing treatment can refine the primaryα-Al phase in A356 alloy

and it has a better primary remelting stability at 650℃.