Wear Properties of B<sub>4</sub>C<sub>p</sub>/AlSi9Mg Composites Prepared by Electromagnetic Stirring

Wang Ziyi; Tan Jianbo

doi:10.15980/j.tzzz.2020.03.018

Views : 0 下载量: 35 CSCD: 0

Export
Share
Collection
Album

Wear Properties of B₄C_p/AlSi9Mg Composites Prepared by Electromagnetic Stirring
Vol. 40, Issue 3, Pages: 313-317(2020)
Published： 2020 ，
DOI： 10.15980/j.tzzz.2020.03.018

扫描看全文

[1]王子一,谭建波.电磁搅拌制备B_4C_p/AlSi9Mg复合材料磨损性能研究[J].特种铸造及有色合金,2020,40(03):313-317.

Wang Ziyi, Tan Jianbo. Wear Properties of B₄C_p/AlSi9Mg Composites Prepared by Electromagnetic Stirring. [J]. Special Casting & Nonferrous Alloys 40(3):313-317(2020)
[1]王子一,谭建波.电磁搅拌制备B_4C_p/AlSi9Mg复合材料磨损性能研究[J].特种铸造及有色合金,2020,40(03):313-317. DOI： 10.15980/j.tzzz.2020.03.018.

Wang Ziyi, Tan Jianbo. Wear Properties of B₄C_p/AlSi9Mg Composites Prepared by Electromagnetic Stirring. [J]. Special Casting & Nonferrous Alloys 40(3):313-317(2020) DOI： 10.15980/j.tzzz.2020.03.018.

摘要

采用电磁搅拌技术制备了B

/Al复合材料

并对B

C颗粒进行了预处理

利用MMW-1A型磨损试验机对复合材料进行磨损试验

研究材料的磨损性能及机制。结果表明

C颗粒预处理可有效去除颗粒中混杂的杂质金属;当电磁搅拌强度为60%

搅拌频率为20Hz

搅拌时间为15min

陶瓷颗粒含量为3.5%时

具有良好的磨损性能。在磨损过程中

随着磨损时间延长

其磨损机理随之变化

由单一的剥层磨损最后变为氧化磨损、粘着磨损以及磨粒磨损等多种制机共同作用。

Abstract

/Al composites were prepared by electromagnetic stirring technology

in which B

C particle were pretreated.The wear properties and mechanism of the composites prepared were investigated by wear test on MMW-1 Awear tester.The results reveal that the impurity metal mixed in the particles can be effectively removed by pretreatment for B

C particles.The composites prepared present the satisfied wear resistance with electric stirring intensity of 60%

stirring frequency of 20 Hz

stirring time of 15 min and particle content of 3.5%.During the wearing process

with the increase of wear time

the wear mechanism is changed from palling wear to the comprehensive effect of oxidative wear

adhesive wear and abrasive wear.