Thermal Deformation Behavior and Constitutive Relation of Ti-48Al-2Nb-2Cr Alloy

Ni Hongming; Dong Xianjuan; Xu Yong; Lu Shiqiang; Gong Siheng

doi:10.15980/j.tzzz.2020.02.026

Views : 0 下载量: 105 CSCD: 3

Export
Share
Collection
Album

Thermal Deformation Behavior and Constitutive Relation of Ti-48Al-2Nb-2Cr Alloy
Vol. 40, Issue 2, Pages: 228-232(2020)
Published： 2020 ，
DOI： 10.15980/j.tzzz.2020.02.026

扫描看全文

[1]倪红明,董显娟,徐勇,鲁世强,龚思恒.Ti-48Al-2Nb-2Cr合金热变形行为及本构关系研究[J].特种铸造及有色合金,2020,40(02):228-232.

Ni Hongming, Dong Xianjuan, Xu Yong, et al. Thermal Deformation Behavior and Constitutive Relation of Ti-48Al-2Nb-2Cr Alloy. [J]. Special Casting & Nonferrous Alloys 40(2):228-232(2020)
[1]倪红明,董显娟,徐勇,鲁世强,龚思恒.Ti-48Al-2Nb-2Cr合金热变形行为及本构关系研究[J].特种铸造及有色合金,2020,40(02):228-232. DOI： 10.15980/j.tzzz.2020.02.026.

Ni Hongming, Dong Xianjuan, Xu Yong, et al. Thermal Deformation Behavior and Constitutive Relation of Ti-48Al-2Nb-2Cr Alloy. [J]. Special Casting & Nonferrous Alloys 40(2):228-232(2020) DOI： 10.15980/j.tzzz.2020.02.026.

摘要

采用Gleeble-1500热力模拟机对铸态Ti-48Al-2Nb-2Cr合金进行高温变形热压缩试验

变形温度范围为1 050～1 200℃

应变速率范围为0.001～0.1s

-1

压缩变形量为60%。研究该合金高温变形温度和应变速率与流变应力之间的关系

计算了合金激活能

并建立了Ti-48Al-2Nb-2Cr合金的Arrhenius本构模型和多元线性回归的本构模型。结果表明

该合金的激活能随温度升高和应变速率增大而增大;Arrhenius本构模型的相关系数为0.982 28

平均相对误差为9.97%

相对误差在10%以内的点只占62.0%;而采用多元线性回归本构模型的相关系数为0.995 66

平均相对误差为4.76%

相对误差在10%以内的点占92.6%

本构精度较高。

Abstract

The as-cast Ti-48Al-2Nb-2Cr alloy was subjected to high temperature hot compressive deformation test by using Gleeble-1500 thermal simulator at 1 050℃to 1 200℃and the strain rate of 0.001 s

-1

to 0.1 s

-1

as well as deformation rate of 60%.The relationship between deformation temperature

strain rate and flow stress during high temperature deformation of the alloy was analyzed.Meanwhile

the active energy of the alloy was calculated.The Arrhenius constitutive model of Ti-48Al-2Nb-2Cr alloy and the constitutive model of multiple linear regression were established.The results reveal that the active energy of the alloy is increased with increasing in temperature and strain rate.The correlation coefficient Rof the Arrhenius constitutive model reaches 0.982 28

and the average relative error is 9.97%.In addition

the relative error within 10% only accounts for 62.0%.The correlation coefficient Rof the constitutive model of Ti-48Al-2Nb-2Cr alloy with multivariate linear regression reaches0.995 66

and the average relative error is 4.76%

meanwhile

the relative error within 10%is 92.6%

presenting a higher constitutive accuracy.