Forming Process and Mechanical Properties of Squeeze Casting A356.2 Aluminum Alloy Engine Mounting Bracket

Chen Yun; Wang Rui; Deng Seng; Liu Kejia; Xia Wanghong

doi:10.15980/j.tzzz.2020.02.014

Views : 0 下载量: 82 CSCD: 1

Export
Share
Collection
Album

Forming Process and Mechanical Properties of Squeeze Casting A356.2 Aluminum Alloy Engine Mounting Bracket
Vol. 40, Issue 2, Pages: 175-178(2020)
Published： 2020 ，
DOI： 10.15980/j.tzzz.2020.02.014

扫描看全文

[1]陈云,汪锐,邓森,刘可佳,夏望红.挤压铸造A356.2铝合金发动机悬置支架的组织与性能[J].特种铸造及有色合金,2020,40(02):175-178.

Chen Yun, Wang Rui, Deng Seng, et al. Forming Process and Mechanical Properties of Squeeze Casting A356.2 Aluminum Alloy Engine Mounting Bracket. [J]. Special Casting & Nonferrous Alloys 40(2):175-178(2020)
[1]陈云,汪锐,邓森,刘可佳,夏望红.挤压铸造A356.2铝合金发动机悬置支架的组织与性能[J].特种铸造及有色合金,2020,40(02):175-178. DOI： 10.15980/j.tzzz.2020.02.014.

Chen Yun, Wang Rui, Deng Seng, et al. Forming Process and Mechanical Properties of Squeeze Casting A356.2 Aluminum Alloy Engine Mounting Bracket. [J]. Special Casting & Nonferrous Alloys 40(2):175-178(2020) DOI： 10.15980/j.tzzz.2020.02.014.

摘要

以挤压铸造A356.2铝合金发动机悬置支架为研究对象

对支架铸态组织、不同固溶时效热处理后的显微组织与力学性能

以及内部缺陷进行了分析研究。结果表明

挤压铸造A356.2铝合金铸态组织由α-Al相和Al-Si共晶组成

晶粒尺寸约为148μm

二次枝晶间距约为20μm;经固溶时效处理后

共晶Si一部分溶入α-Al相中

一部分以粒状、球状形式分布在α-Al晶界;固溶时间、时效温度和时效时间对A356.2合金的力学性能有一定影响。试样经过535℃×6h固溶+8min水淬+170℃×6h时效处理后

抗拉强度为340.5MPa

屈服强度为274.5MPa

伸长率为10%

满足支架整体力学性能要求。

Abstract

The microstructure

mechanical properties under different solid solution and aging conditions and internal defects of the squeeze casting A365.2 aluminum alloy engine mount bracket were investigated.The results reveal that microstructure of the heat-treated A356.2 alloy is composed mainly ofα-Al matrix

eutectic Si phase and Mg

Si phase with a grain size of about 148μm and the secondary dendrite spacing around 20μm.After solution aging treatment

part of the eutectic Si phase is dissolved into theα-Al matrix

and the other is distributed in the form of granular or spherical particle at theα-Al grain boundary.The solution time

aging temperature and aging time can affect the mechanical properties of A356.2.It is found that with solution at 535 ℃ for 6 hand water quenching for 8 min+ aging at 170℃for 6 h

the tensile strength

yield strength and elongation of the squeezing casting aluminum alloy bracket reach 340.5 MPa

274.5 MPa and 10%

respectively

meeting the mechanical properties standard required by the engine bracket.