Simulation and Optimization of Low Pressure Casting Process for C5M4 Aluminum Alloy End Cap
Vol. 39, Issue 8, Pages: 863-866(2019)
Published： 2019 ，
DOI： 10.15980/j.tzzz.2019.08.013

扫描看全文

[1]张雅晴,谭建波.C5M4铝合金端盖低压铸造工艺模拟及优化[J].特种铸造及有色合金,2019,39(08):863-866.

Zhang Yaqing, Tan Jianbo. Simulation and Optimization of Low Pressure Casting Process for C5M4 Aluminum Alloy End Cap. [J]. Special Casting & Nonferrous Alloys 39(8):863-866(2019)
[1]张雅晴,谭建波.C5M4铝合金端盖低压铸造工艺模拟及优化[J].特种铸造及有色合金,2019,39(08):863-866. DOI： 10.15980/j.tzzz.2019.08.013.

Zhang Yaqing, Tan Jianbo. Simulation and Optimization of Low Pressure Casting Process for C5M4 Aluminum Alloy End Cap. [J]. Special Casting & Nonferrous Alloys 39(8):863-866(2019) DOI： 10.15980/j.tzzz.2019.08.013.

摘要

应用ProCAST软件对C5M4铝合金端盖低压铸造工艺进行数值模拟

设计不同浇注系统

在优选浇注方案基础上

采用正交试验研究了浇注温度、模具预热温度、充型压力和充型速度对C5M4端盖低压铸造工艺的影响。通过正交试验

得出最优工艺方案:浇注温度为700℃

模具预热温度为250℃

充型压力为40kPa

充型速度为80mm/s

在优化工艺方案基础上添加冒口

端盖缩松、缩孔体积由75.23cm

降为68.96cm

。

Abstract

The low pressure casting process of the C5M4 end cap was simulated by the ProCAST software.By orthogonal experiments

the effects of pouring temperature

mould preheating temperature

filling pressure and filling speed on the low pressure casting process of C5M4 end cap were analyzed based on the optimized pouring scheme from experiments on different gating systems.Through orthogonal experiment

the optimized technological scheme was presented as pouring temperature of 700℃

mould preheating temperature of 250℃

filling pressure of 40 kPa and filling speed of 80 mm/s.Through adding risers on the basis of the optimized technological parameters

shrinkage porosities of end cap can be reduced obviously from 75.23 cm

to 68.96 cm