Application of New Local Pressurizationin in Solving the Problem of Gas Leakage in Die Castings

Huang Zhiyuan; Zhang Yulong; Zhao Weihong; An Zhaoyong

doi:10.15980/j.tzzz.2019.07.012

Views : 0 下载量: 37 CSCD: 0

Export
Share
Collection
Album

Application of New Local Pressurizationin in Solving the Problem of Gas Leakage in Die Castings
Vol. 39, Issue 7, Pages: 742-744(2019)
Published： 2019 ，
DOI： 10.15980/j.tzzz.2019.07.012

扫描看全文

[1]黄志垣,张玉龙,赵卫红,安肇勇.局部加压技术在解决压铸件漏气问题上的应用[J].特种铸造及有色合金,2019,39(07):742-744.

Huang Zhiyuan, Zhang Yulong, Zhao Weihong, et al. Application of New Local Pressurizationin in Solving the Problem of Gas Leakage in Die Castings. [J]. Special Casting & Nonferrous Alloys 39(7):742-744(2019)
[1]黄志垣,张玉龙,赵卫红,安肇勇.局部加压技术在解决压铸件漏气问题上的应用[J].特种铸造及有色合金,2019,39(07):742-744. DOI： 10.15980/j.tzzz.2019.07.012.

Huang Zhiyuan, Zhang Yulong, Zhao Weihong, et al. Application of New Local Pressurizationin in Solving the Problem of Gas Leakage in Die Castings. [J]. Special Casting & Nonferrous Alloys 39(7):742-744(2019) DOI： 10.15980/j.tzzz.2019.07.012.

摘要

以某发动机摇臂室压铸件的缺陷为研究对象

对其内部缩孔及油道漏气原因进行了分析

并通过采用局部加压技术

改善了铸件的内部缩孔状态。对比发现

使用新一代局部加压技术后

铸件的内部质量更好

油道漏气率大幅降低

其漏气率由原来的18.7%降低到了0.6%。

Abstract

The defects in die-casting rocker arm chamber were investigated

and the origination of the shrinkage and gas leakage was analyzed.The internal shrinkage condition of the rocker arm chamber was improved by applying new local pressurization technology.The results reveal that the quality of the die castings is much better after using new local pressurization

and the oil passage gas leakage rate of the rocker arm chamber is reduced greatly from 18.7%to 0.6%

decreasing greatly cost.