Microstructure and Mechanical Properties of Mould Steels AISI 420 and S136 by Selective Laser Melting Manufacturing

Zhu Xuechao; Wen Shifeng; Wei Qingsong

doi:10.15980/j.tzzz.2019.05.012

Views : 0 下载量: 141 CSCD: 1

Export
Share
Collection
Album

Microstructure and Mechanical Properties of Mould Steels AISI 420 and S136 by Selective Laser Melting Manufacturing
Vol. 39, Issue 5, Pages: 506-510(2019)
Published： 2019 ，
DOI： 10.15980/j.tzzz.2019.05.012

扫描看全文

[1]朱学超,文世峰,魏青松.AISI420与S136模具钢SLM成形组织及性能[J].特种铸造及有色合金,2019,39(05):506-510.

Zhu Xuechao, Wen Shifeng, Wei Qingsong. Microstructure and Mechanical Properties of Mould Steels AISI 420 and S136 by Selective Laser Melting Manufacturing. [J]. Special Casting & Nonferrous Alloys 39(5):506-510(2019)
[1]朱学超,文世峰,魏青松.AISI420与S136模具钢SLM成形组织及性能[J].特种铸造及有色合金,2019,39(05):506-510. DOI： 10.15980/j.tzzz.2019.05.012.

Zhu Xuechao, Wen Shifeng, Wei Qingsong. Microstructure and Mechanical Properties of Mould Steels AISI 420 and S136 by Selective Laser Melting Manufacturing. [J]. Special Casting & Nonferrous Alloys 39(5):506-510(2019) DOI： 10.15980/j.tzzz.2019.05.012.

摘要

采用激光选区熔化（SLM）技术分别成形注塑模具钢AISI420和S136

对两种模具钢的相组成、微观组织、显微硬度、抗拉强度和摩擦磨损性能等进行了研究。结果表明

SLM成形的AISI420具有更高的合金元素固溶度

合金固溶强化使得AISI420比S136具有更高的强度和伸长率

其强度和伸长率分别为1 234.13MPa、14.63%和642.89MPa、9.76%;由于S136中的C含量较高

在激光的快速冷却作用下

S136比AISI420更易产生马氏体组织

因此拥有更高的硬度和较低的磨损率

二者硬度（HV

）和磨损率分别为589、3.28×10

-6

·N

-1

·m

-1

493.78、4.12×10

-6

·N

-1

·m

-1

。

Abstract

Injection tool steels AISI 420 and S136 samples were fabricated by selective laser melting（SLM）technique.The phase composition

microstructure

microhardness

tensile strength and wear resistance of two tool steels were investigated systematically.The results show that SLM-processed AISI 420 samples have a higher solid solubility of the alloying elements.Due to the solid solution strengthening of the alloying elements

the AISI420 samples present the higher tensile strength and elongation than that of S136 samples.Tensile strength and elongation of the SLM-processed AISI 420 and S136 reach 1 234.13 MPa

14.63% and 642.89 MPa

9.76%

respectively.Due to the higher C content in S136

the martensitic transformation is more easily generated in the S136 samples under the laser-induced large solidification rate as compared to AISI 420 samples.The higher hardness and lower wear rate ware obtained for the SLM-processed S136 samples.Microhardness and wear rate of the SLM-processed S136 and AISI 420 samples reach 589 HV

3.28×10

-6

·N

-1

·m

-1

and 493.78 HV

4.12×10

-6

·N

-1

·m