Effects of Melt Treatment on ZL114AAlloy Gypsum Mold Investment Castings
Vol. 38, Issue 10, Pages: 1096-1099(2018)
Published： 2018 ，
DOI： 10.15980/j.tzzz.2018.10.015

扫描看全文

[1]王狂飞,张锦志,李早,周志杰,吕三雷,刘宝忠.熔体处理对ZL114A合金石膏型精铸件的影响[J].特种铸造及有色合金,2018,38(10):1096-1099.

Wang Kuangfei, Zhang Jinzhi, Li Zao, et al. Effects of Melt Treatment on ZL114AAlloy Gypsum Mold Investment Castings. [J]. Special Casting & Nonferrous Alloys 38(10):1096-1099(2018)
[1]王狂飞,张锦志,李早,周志杰,吕三雷,刘宝忠.熔体处理对ZL114A合金石膏型精铸件的影响[J].特种铸造及有色合金,2018,38(10):1096-1099. DOI： 10.15980/j.tzzz.2018.10.015.

Wang Kuangfei, Zhang Jinzhi, Li Zao, et al. Effects of Melt Treatment on ZL114AAlloy Gypsum Mold Investment Castings. [J]. Special Casting & Nonferrous Alloys 38(10):1096-1099(2018) DOI： 10.15980/j.tzzz.2018.10.015.

摘要

通过力学性能测试和显微组织观察

研究了熔体处理对ZL114A合金石膏型精铸件缩松缺陷和力学性能的影响。结果表明

变质试样力学性能较未变质试样出现大幅下降与缩松增多有关。Sr的加入相当于改变了合金凝固范围

使试样倾向于糊状凝固;而变质剂和熔体反应形成的夹杂未被处理干净

以及熔体处理时间过长

均加剧了气缩松的形成。

Abstract

Through mechanical properties test and microstructural observation

effects of melt treatment on porosities and mechanical properties of gypsum mold casting ZL114 Aalloy sample were investigated.The results show that the mechanical properties of the modified samples are decreased significantly compared with those of the unmodified ones

which are related to the increase of shrinkage.The addition of Sr is equivalent to changing the solidification range of the melts so that the sample tends to be solidified in the mushy zone

and the inclusion formed by the reaction of the modifier and melts is not treated fully

and the melt treatment time is longer

which are responsible for the formation of "gas shrinkage".