Optimization of Permanent Mold Casting Processes for Shrinkage Porosity Reduction in Cu-45Ag Alloy by Simulation and Taguchi Method

Meng Zhijun; Wang Ye; Niu Lianjie; Xu Hongyu; Hu Maoliang; Ji Zesheng

doi:10.15980/j.tzzz.2018.10.006

Views : 0 下载量: 125 CSCD: 1

Export
Share
Collection
Album

Optimization of Permanent Mold Casting Processes for Shrinkage Porosity Reduction in Cu-45Ag Alloy by Simulation and Taguchi Method
Vol. 38, Issue 10, Pages: 1064-1067(2018)
Published： 2018 ，
DOI： 10.15980/j.tzzz.2018.10.006

扫描看全文

[1]孟志军,王晔,牛连杰,许红雨,胡茂良,吉泽升.基于田口方法的Cu-45Ag合金金属型铸造过程仿真及工艺优化[J].特种铸造及有色合金,2018,38(10):1064-1067.

Meng Zhijun, Wang Ye, Niu Lianjie, et al. Optimization of Permanent Mold Casting Processes for Shrinkage Porosity Reduction in Cu-45Ag Alloy by Simulation and Taguchi Method. [J]. Special Casting & Nonferrous Alloys 38(10):1064-1067(2018)
[1]孟志军,王晔,牛连杰,许红雨,胡茂良,吉泽升.基于田口方法的Cu-45Ag合金金属型铸造过程仿真及工艺优化[J].特种铸造及有色合金,2018,38(10):1064-1067. DOI： 10.15980/j.tzzz.2018.10.006.

Meng Zhijun, Wang Ye, Niu Lianjie, et al. Optimization of Permanent Mold Casting Processes for Shrinkage Porosity Reduction in Cu-45Ag Alloy by Simulation and Taguchi Method. [J]. Special Casting & Nonferrous Alloys 38(10):1064-1067(2018) DOI： 10.15980/j.tzzz.2018.10.006.

摘要

通过田口方法（DOE）、数值模拟和浇注试验相结合

研究了浇注温度、铸型温度和涂料厚度对宏观缩孔体积率的影响

并对金属型铸造Cu-Ag合金工艺进行了优化。通过实际浇注试验

对模拟结果的可靠性以及田口方法分析得到的置信区间进行验证

获得了最优工艺方案:浇注温度为1 100℃、铸型温度为200℃、涂料厚度为1.5mm。

Abstract

The shrinkage porosity in Cu-Ag binary alloy fabricated by permanent mold casting was analyzed by the Design of Experiment（DOE）based on Taguchi method

numerical simulation and casting experiment.The effects of processing parameters

such as pouring temperature

mold temperature and coating thickness

were analyzed on quality of shrinkage porosity ratio of Cu-Ag alloy.The numerical experiments with different processes were designed by Taguchi method and the simulated results were analyzed based on the signal-to-noise ratio（S/N）and analysis of variance（ANOVA）.The influence of various process parameters on shrinkage porosity was described

and optimization of processing parameters was also proposed.Then the validity of the method and its confidence interval were confirmed by the verification test.The results indicate that the optimized process parameters are presented as follow:pouring temperature of 1 100℃

mold temperature of 200℃and the coating thickness of 1.5 mm.