Effectsof Projectile Size on Microstructure and Properties of GH4169 Surface by Wet Shot Peening
Vol. 38, Issue 6, Pages: 674-677(2018)
Published： 2018 ，
DOI： 10.15980/j.tzzz.2018.06.026

扫描看全文

[1]郭胜华,郑海忠,程世平,舒小勇,李贵发.喷丸尺寸对GH4169表层湿喷丸组织与性能的影响[J].特种铸造及有色合金,2018,38(06):674-677.

Guo Shenghua, Zheng Haizhong, Cheng Shiping, et al. Effectsof Projectile Size on Microstructure and Properties of GH4169 Surface by Wet Shot Peening. [J]. Special Casting & Nonferrous Alloys 38(6):674-677(2018)
[1]郭胜华,郑海忠,程世平,舒小勇,李贵发.喷丸尺寸对GH4169表层湿喷丸组织与性能的影响[J].特种铸造及有色合金,2018,38(06):674-677. DOI： 10.15980/j.tzzz.2018.06.026.

Guo Shenghua, Zheng Haizhong, Cheng Shiping, et al. Effectsof Projectile Size on Microstructure and Properties of GH4169 Surface by Wet Shot Peening. [J]. Special Casting & Nonferrous Alloys 38(6):674-677(2018) DOI： 10.15980/j.tzzz.2018.06.026.

摘要

利用湿喷丸对GH4169合金进行表面处理

研究了不同喷丸直径（1、2、4mm）对合金表面形貌、表层显微组织、表面粗糙度和显微硬度的影响。结果表明

随着喷丸直径增加

合金表面完整性降低

而喷丸作用层厚度、显微硬度、表面粗糙度都随之增加。当喷丸直径为4mm、作用时间为5min时

喷丸作用层厚度和表面显微硬度（HV）最大

分别为320μm和356。

Abstract

The surface of GH4169 alloy was treated by wet shot peening

and effects of shot peening projectile size on the surface morphology

microstructure

roughness and micro-hardness of GH4169 alloys were investigated.The results show that the surface integrity of the alloy is decreased with the increase of the projectile size

while the shot peening layer

the microhardness and the surface roughness are increased.With 4 mm wet shot peening for 5 min

the shot peening effect layer and surface micro-hardness reach 320μm and 356 HV

respectively.