Properties of MIG Welding AZ91D Cast Magnesium Alloy with Aluminum based Welding Wire and Its Effect
Vol. 38, Issue 4, Pages: 425-428(2018)
Published： 2018 ，
DOI： 10.15980/j.tzzz.2018.04.021

扫描看全文

[1]毛津,侯击波,许凯,刘雅鑫.采用铝基焊丝MIG焊接AZ91D镁合金的性能[J].特种铸造及有色合金,2018,38(04):425-428.

Mao Jin, Hou Jibo, Xu Kai, et al. Properties of MIG Welding AZ91D Cast Magnesium Alloy with Aluminum based Welding Wire and Its Effect. [J]. Special Casting & Nonferrous Alloys 38(4):425-428(2018)
[1]毛津,侯击波,许凯,刘雅鑫.采用铝基焊丝MIG焊接AZ91D镁合金的性能[J].特种铸造及有色合金,2018,38(04):425-428. DOI： 10.15980/j.tzzz.2018.04.021.

Mao Jin, Hou Jibo, Xu Kai, et al. Properties of MIG Welding AZ91D Cast Magnesium Alloy with Aluminum based Welding Wire and Its Effect. [J]. Special Casting & Nonferrous Alloys 38(4):425-428(2018) DOI： 10.15980/j.tzzz.2018.04.021.

摘要

研究了采用φ1.2mm的S301和φ1.6mm的ER5356铝基焊丝MIG焊接AZ91D镁合金的可焊接性。试验表明

在各自的焊接规范内两种焊丝均可完成有效焊接

焊缝中存在大量的Mg

脆硬相

严重影响了焊缝的力学性能。焊缝中Mg基固溶体和Mg-Al脆硬相的相对含量与局部Mg和Al的含量相关。通过向焊缝过渡锌合金

发现Zn元素可以明显减少焊缝中的Mg

相

析出MgZn

新相

促进了Mg基固溶体的生长

最终提高了焊缝的综合力学性能。

Abstract

The properties of MIG welding AZ91 Dcast magnesium alloy with φ1.2 mm S301 and φ1.6 mm ER5356 aluminum wire were investigated.The results reveal that two kinds of welding wires can be welded effectively in each welding specification

and a large number of Mg

brittle phases can be observed in the welded zone

which affect seriously the mechanical properties of the welded zone.The relative content of the Mg based solid solution and the Mg-Al brittle phase in the welded zone is related to the ratio of local Mg and Al.By adding zinc alloy to the welding zone

it is found that zinc can reduce greadly the Mg

phase in the welded zone

and MgZn

new phase is precipitated

which promote the growth of magnesium based solid solution.Finally

the comprehensive mechanical properties of the welding zone are improved.

关键词

铝基焊丝Zn箔Mg17Al17相MgZn2相

Keywords

Aluminum Base Welding WireZinc FoilMg17Al12 PhaseMgZn2 Phase