Influence of Ultrasonic Vibration Treatment on Fe-enriched Phases and Mechanical Properties of Al-14Si-xFe-yMn Alloys

Lin Chong; Wu Shusen; LüShulin; Wu Hebao

doi:10.15980/j.tzzz.2018.01.028

Views : 0 下载量: 44 CSCD: 1

Export
Share
Collection
Album

Influence of Ultrasonic Vibration Treatment on Fe-enriched Phases and Mechanical Properties of Al-14Si-xFe-yMn Alloys
Vol. 38, Issue 1, Pages: 105-109(2018)
Published： 2018 ，
DOI： 10.15980/j.tzzz.2018.01.028

扫描看全文

[1]林冲,吴树森,吕书林,吴和保.超声对Al-14Si-xFe-yMn合金富Fe相和性能的影响[J].特种铸造及有色合金,2018,38(01):105-109.

Lin Chong, Wu Shusen, LüShulin, et al. Influence of Ultrasonic Vibration Treatment on Fe-enriched Phases and Mechanical Properties of Al-14Si-xFe-yMn Alloys. [J]. Special Casting & Nonferrous Alloys 38(1):105-109(2018)
[1]林冲,吴树森,吕书林,吴和保.超声对Al-14Si-xFe-yMn合金富Fe相和性能的影响[J].特种铸造及有色合金,2018,38(01):105-109. DOI： 10.15980/j.tzzz.2018.01.028.

Lin Chong, Wu Shusen, LüShulin, et al. Influence of Ultrasonic Vibration Treatment on Fe-enriched Phases and Mechanical Properties of Al-14Si-xFe-yMn Alloys. [J]. Special Casting & Nonferrous Alloys 38(1):105-109(2018) DOI： 10.15980/j.tzzz.2018.01.028.

摘要

研究了超声处理对Al-14Si-xFe-yMn（x=1

y/x=0.2）合金中富Fe相和力学性能的影响。结果表明

无超声处理时

Al-14Si-1Fe-0.2Mn合金组织中含大量针状β-Al

FeSi相。当Fe含量达到或超过2%时

板条状δ-Al

FeSi

相出现。超声处理不仅使得粗大β-Al

FeSi和δ-Al

FeSi

相细化

还促进了不规则多边形α-Al

（Fe

Mn）

相的生成。α相在超声处理结束后发生了Ostwald熟化

即随着Fe含量的增加

α相向着粗大近球形演变。在同等条件下

相比无超声处理的试样

有超声处理的试样室温强度显著提高。超声处理后合金的高温强度也略有增加。

Abstract

The influence of ultrasonic vibration treatment（UVT）on the Fe-enriched phases and mechanical properties of Al-14Si-xFe-yMn（x=1

y/x=0.2）alloys were investigated.The results show that the long-needle-likeβ-Al

FeSi phase can be generated in the Al-14Si-1Fe-0.2Mn alloy without UVT.When the iron content in the alloy is equal or greater than 2%

both of the long-needle likeβ-Al

FeSi phase and coarse plate-likeδ-Al

FeSi

phase appear.The coarseβ-Al

FeSi andδ-Al

FeSi

phase can be refined to a certain extent after UVT.In addition

the formation of irregular polygonalα-Al

（Fe

Mn）

phase is also promoted.Ostwald ripening of theα-Al

（Fe

Mn）

phase takes place during the solidification process after UVT.Some grains ofα-Al

（Fe

Mn）

phase are close to spherical particles when the iron content is increased.The room temperature tensile strength of the alloy with UVT is improved significantly compared to that without UVT.The tensile strength at 350℃is also improved slightly.