Microstructure and Wear Properties of SiC<sub>p</sub>/Ni35 Coatings by Laser Cladding

Ding Zizheng; Pan Chenggang; Chang Qingming; Wu Qiong

doi:10.15980/j.tzzz.2017.08.022

Views : 0 下载量: 128 CSCD: 4

Export
Share
Collection
Album

Microstructure and Wear Properties of SiC_p/Ni35 Coatings by Laser Cladding
Vol. 37, Issue 8, Pages: 886-890(2017)
Published： 2017 ，
DOI： 10.15980/j.tzzz.2017.08.022

扫描看全文

[1]丁紫正,潘成刚,常庆明,吴琼.激光熔覆SiC_p/Ni35覆层组织与磨损性能研究[J].特种铸造及有色合金,2017,37(08):886-890.

Ding Zizheng, Pan Chenggang, Chang Qingming, et al. Microstructure and Wear Properties of SiC_p/Ni35 Coatings by Laser Cladding. [J]. Special Casting & Nonferrous Alloys 37(8):886-890(2017)
[1]丁紫正,潘成刚,常庆明,吴琼.激光熔覆SiC_p/Ni35覆层组织与磨损性能研究[J].特种铸造及有色合金,2017,37(08):886-890. DOI： 10.15980/j.tzzz.2017.08.022.

Ding Zizheng, Pan Chenggang, Chang Qingming, et al. Microstructure and Wear Properties of SiC_p/Ni35 Coatings by Laser Cladding. [J]. Special Casting & Nonferrous Alloys 37(8):886-890(2017) DOI： 10.15980/j.tzzz.2017.08.022.

摘要

为提高热作模具钢H13钢的耐磨性

采用激光熔覆在H13钢表面制备了SiC

/Ni35熔覆层。用XRD、OM、SEM和EDS对熔覆层的物相、组织和成分进行了分析;测试了熔覆层的显微硬度;用高温磨损试验机测试了熔覆层的常温和高温耐磨性能。结果表明

熔覆层由γ-Ni（Fe）固溶体、增强相M

以及硼化物、硅化物和石墨构成。熔覆层的显微硬度、常温及高温摩擦性能都比H13钢有显著提高。

Abstract

In order to improve the wear resistance of H13 steel

SiC

/Ni35 coatings on H13 surface were prepared by laser cladding.Coating phases

microstructure and elements in the coating were analyzed by XRD

SEM and EDS.Microhardness of coating was tested by microharness tester.The room temperature and high temperature wear resistances of coatings were tested by high temperature wear tester.The results reveal that coating is composed of solid solution of Ni

reinforcing phase M

borides

silicides and graphites.Coating exhibits the better microhardness

room temperature and high temperature wear resistance than H13 steel.