Fabrication of Lateral Compound Cu/Al Composites by Conclad Continuous Extrusion

Ling Cong; Zhong Yi; Chen Yegao; Wang Fei; Gao Xiaolei

doi:10.15980/j.tzzz.2017.01.024

Views : 0 下载量: 112 CSCD: 2

Export
Share
Collection
Album

Fabrication of Lateral Compound Cu/Al Composites by Conclad Continuous Extrusion
Vol. 37, Issue 1, Pages: 89-93(2017)
Published： 2017 ，
DOI： 10.15980/j.tzzz.2017.01.024

扫描看全文

[1]凌聪,钟毅,陈业高,王飞,郜晓雷.Conclad连续挤压法制备侧向复合型Cu/Al复合材料[J].特种铸造及有色合金,2017,37(01):89-93.

Ling Cong, Zhong Yi, Chen Yegao, et al. Fabrication of Lateral Compound Cu/Al Composites by Conclad Continuous Extrusion. [J]. Special Casting & Nonferrous Alloys 37(1):89-93(2017)
[1]凌聪,钟毅,陈业高,王飞,郜晓雷.Conclad连续挤压法制备侧向复合型Cu/Al复合材料[J].特种铸造及有色合金,2017,37(01):89-93. DOI： 10.15980/j.tzzz.2017.01.024.

Ling Cong, Zhong Yi, Chen Yegao, et al. Fabrication of Lateral Compound Cu/Al Composites by Conclad Continuous Extrusion. [J]. Special Casting & Nonferrous Alloys 37(1):89-93(2017) DOI： 10.15980/j.tzzz.2017.01.024.

摘要

通过Conclad连续挤压法

在挤压温度为500℃下制备出了界面平直度较好

界面层厚度为93μm

界面结合强度高的侧向复合型Cu/Al复合材料。对复合材料界面的力学性能、界面形貌及微观组织进行分析

可知越靠近界面处硬度越高

界面层的抗拉强度为48 MPa

复合界面层存在除铜基体和铝基体以外的金属间化合物

排序从铜基一侧到铝基一侧依次为Cu

、CuAl和CuAl

。而CuAl2是一种脆性相

它的存在容易引起界面结合处出现断裂现象。

Abstract

The lateral compound Cu/Al composites were fabricated by Conclad continuous extrusion at500 ℃

which has a relatively good interface straightness

thickness of the intermetallic compound of93μm and the higher interface bonding strength.The mechanical properties

interface morphology and microstructure of the composites were analyzed.The results indicate that the hardness is inceased significantly nearby the interface

and the tensile strength of interface reaches 48 MPa.The interface intermetallic compand can be observed in compound interface

which is Cu

、CuAl and CuAl

phase form copper side to aluminum side

besides of the copper matrix and aluminum substrate.Fracture is easy to appear in the interface because of the presence of CuAl

brittle phase.