Effects of Isothermal Heat Treatment on Microstructural Evolution of ZA63 Magnesium Alloy

Huang Xiaofeng; Li Ya; Zhang Yu; Ma Zhenduo; Ma Ying; Li Yuandong; Chen Tijun

doi:10.15980/j.tzzz.2016.12.010

Views : 0 下载量: 129 CSCD: 1

Export
Share
Collection
Album

Effects of Isothermal Heat Treatment on Microstructural Evolution of ZA63 Magnesium Alloy
Vol. 36, Issue 12, Pages: 1274-1278(2016)
Published： 2016 ，
DOI： 10.15980/j.tzzz.2016.12.010

扫描看全文

[1]黄晓锋,李雅,张玉,马振铎,马颖,李元东,陈体军.等温热处理对ZA63镁合金半固态组织演变的影响[J].特种铸造及有色合金,2016,36(12):1274-1278.

Huang Xiaofeng, Li Ya, Zhang Yu, et al. Effects of Isothermal Heat Treatment on Microstructural Evolution of ZA63 Magnesium Alloy. [J]. Special Casting & Nonferrous Alloys 36(12):1274-1278(2016)
[1]黄晓锋,李雅,张玉,马振铎,马颖,李元东,陈体军.等温热处理对ZA63镁合金半固态组织演变的影响[J].特种铸造及有色合金,2016,36(12):1274-1278. DOI： 10.15980/j.tzzz.2016.12.010.

Huang Xiaofeng, Li Ya, Zhang Yu, et al. Effects of Isothermal Heat Treatment on Microstructural Evolution of ZA63 Magnesium Alloy. [J]. Special Casting & Nonferrous Alloys 36(12):1274-1278(2016) DOI： 10.15980/j.tzzz.2016.12.010.

摘要

采用等温热处理法对ZA63合金在不同的保温温度及保温时间下的半固态组织的演变过程和机理进行了研究。结果表明

通过半固态等温热处理能够制备ZA63非枝晶组织

并获得细小、分布均匀的球状颗粒。非枝晶组织演变经历了粗化、枝晶分离、球化以及晶粒的合并和长大4个过程。ZA63合金半固态触变成形最适合的等温热处理工艺是590℃×20min

平均晶粒尺寸、圆整度和固相率分别为59.16μm、1.5和43%。

Abstract

The semi-solid non-dendritic microstructure evolution and mechanism of ZA63 magnesium alloy at varied holding temperature and time were investigated by isothermal heat-treatment.The results show that ZA63 alloy with the non-dendritic microstructure can be prepared by semi-solid isothermal heat-treatment

and fine spherical particles with uniform distribution can be obtained.The evolution of non-dendritic microstructure has undergone coarsening

dendrite separation

spheroidization and mergence growth.The optimal heat treatment parameters are reheating at 590 ℃for 20 min for semi-solid thixoforming of the alloy

where the grain size

roundness and solid fraction reach 59.16μm

1.5and43%

respectively.