Numerical Simulation of A356 Truss Core Panels by Low Pressure Investment Casting
Vol. 36, Issue 11, Pages: 1175-1177(2016)
Published： 2016 ，
DOI： 10.15980/j.tzzz.2016.11.016

扫描看全文

[1]董多,朱冬冬,贺庆,周兆忠,倪成员,魏尊杰.A356合金3D Kagome点阵夹芯板低压熔模铸造工艺[J].特种铸造及有色合金,2016,36(11):1175-1177.

Dong Duo, Zhu Dongdong, He Qing, et al. Numerical Simulation of A356 Truss Core Panels by Low Pressure Investment Casting. [J]. Special Casting & Nonferrous Alloys 36(11):1175-1177(2016)
[1]董多,朱冬冬,贺庆,周兆忠,倪成员,魏尊杰.A356合金3D Kagome点阵夹芯板低压熔模铸造工艺[J].特种铸造及有色合金,2016,36(11):1175-1177. DOI： 10.15980/j.tzzz.2016.11.016.

Dong Duo, Zhu Dongdong, He Qing, et al. Numerical Simulation of A356 Truss Core Panels by Low Pressure Investment Casting. [J]. Special Casting & Nonferrous Alloys 36(11):1175-1177(2016) DOI： 10.15980/j.tzzz.2016.11.016.

摘要

以3D-Kagome点阵夹芯板为研究对象

采用Anycasting软件对A356合金点阵夹芯板的低压熔模铸造过程进行数值模拟

研究了浇注系统及主要的工艺参数对A356合金点阵夹芯板成形的影响

并在此基础上进行了工艺优化。结果表明

随着浇注温度提高

金属液的充型能力增加

缺陷减少

但当温度超过770℃时

缩松、缩孔缺陷有增加的趋势。通过模拟计算

确定了点阵夹芯板最佳浇注工艺:浇注温度为770℃

型壳预热温度为200℃

充型速度为40mm/s

并将模拟试验结果进行试验验证

表明该工艺切实可行。

Abstract

The effects of gating system and main processing parameters on forming of A356 truss core panel produced by low pressure investment casting process have been simulated by the Anycasting software.And optimization of processing parameters has been carried out based on analysis of the simulation results.The results show that with the increase of pouring temperature

filling ability of liquid metal is increased and the defects in castings are reduced.However

with the pouring temperature more than 770℃

shrinkage porosities（holes）are increased slightly.Based on the simulated results

the optimized process parameters are presented as follows:pouring temperature of 770 ℃

shell preheat temperature of 200 ℃ and filling velocity of 40mm/s.Then the validity of proposed results has been confirmed by the practical production.