Microstructure and Properties of Squeezing Casting Al-6.4Cu-0.4Mn Alloy
Vol. 36, Issue 10, Pages: 1069-1074(2016)
Published： 2016 ，
DOI： 10.15980/j.tzzz.2016.10.017

扫描看全文

[1]高文林,孙进宝,王海龙,罗传彪,孙刚,王长顺,李宏伟,陆政.挤压铸造Al-6.4Cu-0.4Mn合金轮毂的组织与性能[J].特种铸造及有色合金,2016,36(10):1069-1074.

Gao Wenlin, Sun Jinbao, Wang Hailong, et al. Microstructure and Properties of Squeezing Casting Al-6.4Cu-0.4Mn Alloy. [J]. Special Casting & Nonferrous Alloys 36(10):1069-1074(2016)
[1]高文林,孙进宝,王海龙,罗传彪,孙刚,王长顺,李宏伟,陆政.挤压铸造Al-6.4Cu-0.4Mn合金轮毂的组织与性能[J].特种铸造及有色合金,2016,36(10):1069-1074. DOI： 10.15980/j.tzzz.2016.10.017.

Gao Wenlin, Sun Jinbao, Wang Hailong, et al. Microstructure and Properties of Squeezing Casting Al-6.4Cu-0.4Mn Alloy. [J]. Special Casting & Nonferrous Alloys 36(10):1069-1074(2016) DOI： 10.15980/j.tzzz.2016.10.017.

摘要

通过金相组织观察（OM）、扫描电镜（SEM）、透射电镜（TEM）、室温力学性能测试等手段

研究了一种Al-6.4Cu-0.4Mn中强高韧挤压铸造铝合金

同时利用挤压铸造与常规铸造制备了负重轮轮毂

并对比研究了该合金挤压铸造与常规铸造条件下组织、性能的变化情况。结果表明

新合金挤压铸造成形过程中共形成固相区、固液区、液固区以及液体区4个凝固区域;新合金挤压铸造后的显微组织反偏析现象严重

等轴晶程度较高

由铸造组织与变形组织共同组成;新合金挤压铸造成形后经固溶时效热处理

其抗拉强度与伸长率显著优于常规铸造工艺性能

分别达到468 MPa与16.2%。

Abstract

A new Al-6.4Cu-0.4Mn medium strength aluminum alloy was investigated by optical microscope（OM）

scanning electron microscope（SEM）

transmission electron microscopy（TEM）

tensile testing and electric conductivity testing.The loading wheel hub of the alloy prepared was produced by squeezing casting and conventional casting process to analyze comparatively microstructure and mechanical properties of the alloy at different casting process.The results reveal that the solidification state of the new alloy is composed of solid phase zone

solid-liquid phase zone

liquid-solid zone and liquid zone.Microstructure of the squeezing casting new alloy consists of as-cast and deformation structure with serious inverse segregation and high level isometric crystal.Tensile test indicates that strength and elongation of the squeezing casting Al-6.4Cu-0.4Mn aluminum alloy are increased obviously after solution and aging treatment process compared with those of conventional casting process

reaching 468 MPa and16.2%

respectively.