Influence of Plunger Temperature on Uniformity of Microstructure of Semi-solid Squeeze Casting 7075 Alloy

Tan Jianbo; Liu Xueping; Li Lixin

doi:10.15980/j.tzzz.2016.10.012

Views : 0 下载量: 129 CSCD: 1

Export
Share
Collection
Album

Influence of Plunger Temperature on Uniformity of Microstructure of Semi-solid Squeeze Casting 7075 Alloy
Vol. 36, Issue 10, Pages: 1054-1056(2016)
Published： 2016 ，
DOI： 10.15980/j.tzzz.2016.10.012

扫描看全文

[1]谭建波,刘雪萍,李立新.压头温度对挤压铸造7075半固态组织均匀性的影响[J].特种铸造及有色合金,2016,36(10):1054-1056.

Tan Jianbo, Liu Xueping, Li Lixin. Influence of Plunger Temperature on Uniformity of Microstructure of Semi-solid Squeeze Casting 7075 Alloy. [J]. Special Casting & Nonferrous Alloys 36(10):1054-1056(2016)
[1]谭建波,刘雪萍,李立新.压头温度对挤压铸造7075半固态组织均匀性的影响[J].特种铸造及有色合金,2016,36(10):1054-1056. DOI： 10.15980/j.tzzz.2016.10.012.

Tan Jianbo, Liu Xueping, Li Lixin. Influence of Plunger Temperature on Uniformity of Microstructure of Semi-solid Squeeze Casting 7075 Alloy. [J]. Special Casting & Nonferrous Alloys 36(10):1054-1056(2016) DOI： 10.15980/j.tzzz.2016.10.012.

摘要

应用DEFORM-3D软件对7075铝合金半固态挤压铸造充型过程进行了模拟

研究了压头预热温度对7075铝合金杯形件充型过程的影响。在模拟的基础上

利用压力机及杯形试验模具

进行了半固态7075铝合金流变挤压铸造成形

分析了压头预热温度对7075铝合金杯形件半固态挤压铸造组织均匀性的影响。模拟和试验结果表明

压头预热温度越高

充型越平稳;在合金温度为628℃

成形比压为50 MPa

成形速度为3.5mm/s的条件下

随着压头预热温度的增加

杯形件的液相偏析度减小

组织更加均匀。当压头温度为400℃时

杯形件的液相偏析度最小

为14.02%。

Abstract

The semi-solid squeeze casting process for 7075 aluminum alloy was simulated by the DEFORM-3Dsoftware to understand influence of plunger preheating temperature on the forming process of cup part.According to the simulated results

the squeeze casting forming of the part was carried out to analyze influence of plunger preheating temperature on the uniformity of microstructure by means of press machine and cup mould.The results show that the filling stability is improved with increasing in plunger pre-heating temperature.At 628 ℃for 50 MPa and 3.5mm/s

the segregation degree of liquid phase of cup part is decreased

and microstructure uniformity is improved increasingly with the increase of plunger preheating temperature.The minimal segregation degree is 14.02% with plunger preheating temperature at 400 ℃.