Temperature and Porosity Prediction Algorithm during Casting Solidification Process and Software Development
Vol. 36, Issue 8, Pages: 803-806(2016)
Published： 2016 ，
DOI： 10.15980/j.tzzz.2016.08.006

扫描看全文

[1]杨曼云,迟毅林.温度场模拟及缩孔缩松预测算法研究与实现[J].特种铸造及有色合金,2016,36(08):803-806.

Yang Manyun, Chi Yilin. Temperature and Porosity Prediction Algorithm during Casting Solidification Process and Software Development. [J]. Special Casting & Nonferrous Alloys 36(8):803-806(2016)
[1]杨曼云,迟毅林.温度场模拟及缩孔缩松预测算法研究与实现[J].特种铸造及有色合金,2016,36(08):803-806. DOI： 10.15980/j.tzzz.2016.08.006.

Yang Manyun, Chi Yilin. Temperature and Porosity Prediction Algorithm during Casting Solidification Process and Software Development. [J]. Special Casting & Nonferrous Alloys 36(8):803-806(2016) DOI： 10.15980/j.tzzz.2016.08.006.

摘要

对铸造凝固过程温度场模拟及缩孔、缩松缺陷预测算法进行了研究

并应用于SIMU-CAST铸造凝固过程模拟软件研发。软件能基于有限单元法进行凝固过程温度场、缩孔、缩松等铸造缺陷的数值模拟。模拟过程充分考虑材料和边界条件等参数的非线性特征

并考虑结晶潜热的处理。同时对铸件缩孔、缩松预测结果和ProCAST软件计算结果进行对比

验证了所开发软件的准确性。

Abstract

Numerical simulation of temperature and porosity prediction algorithm during casting solidification process was analyzed to develop the SIMU-CAST software.The software can predict temperature field and casting defects

such as shrinkage porosity（holes）based on FEM method

where non-linear features of material characteristics and boundary condition as well as latent heat treatment are taken into account.The simulated result of shrinkage porosity by the self-developed software was compared with that of one by the ProCAST software.The comparative result is satisfied.

关键词

铸造凝固温度场模拟缩孔缩松预测

Keywords

Casting SolidificationTemperature PredictionPorosity Prediction