Effects of Heat Treatment on Microstructure and Mechanical Properties of the 2A14/A390 Aluminum Composites

Jiang Yinfang; Qian Junkang; Wan Li; Xu Ruozhen; Yang Qing; Wang Kewei; Liu Zhen

doi:10.15980/j.tzzz.2016.04.023

Views : 0 下载量: 110 CSCD: 0

Export
Share
Collection
Album

Effects of Heat Treatment on Microstructure and Mechanical Properties of the 2A14/A390 Aluminum Composites
Vol. 36, Issue 4, Pages: 416-418(2016)
Published： 2016 ，
DOI： 10.15980/j.tzzz.2016.04.023

扫描看全文

[1]姜银方,钱俊康,万里,许若震,杨青,王科委,刘振.2A14/A390复合材料热处理组织和性能研究[J].特种铸造及有色合金,2016,36(04):416-418.

Jiang Yinfang, Qian Junkang, Wan Li, et al. Effects of Heat Treatment on Microstructure and Mechanical Properties of the 2A14/A390 Aluminum Composites. [J]. Special Casting & Nonferrous Alloys 36(4):416-418(2016)
[1]姜银方,钱俊康,万里,许若震,杨青,王科委,刘振.2A14/A390复合材料热处理组织和性能研究[J].特种铸造及有色合金,2016,36(04):416-418. DOI： 10.15980/j.tzzz.2016.04.023.

Jiang Yinfang, Qian Junkang, Wan Li, et al. Effects of Heat Treatment on Microstructure and Mechanical Properties of the 2A14/A390 Aluminum Composites. [J]. Special Casting & Nonferrous Alloys 36(4):416-418(2016) DOI： 10.15980/j.tzzz.2016.04.023.

摘要

对铝合金2A14和A390复合材料进行热处理并研究其组织性能。试验中采用热挤压复合铸造技术使得两种金属实现冶金结合

经过固溶热处理后对双金属复合界面的显微组织、显微硬度及结合强度进行测试;并对热处理工艺参数进行分析研究

发现最佳的热处理温度为500℃

固溶4h。

Abstract

Effects of the heat treatment on the microstructure and mechanical properties of 2A14/A390 composites were analyzed.2A14/A390 composites were prepared by hot extrusion combining with casting technology

and the composites prepared were treated by solid solution

and microstructure

microhardness and bonding strength of the composites after solid solution treatment were investigated.The results show that with solid solution at 500℃for 4h

the composites have desirable microstructure and mechanical properties.