Fracture Failure Analysis and Prevention of Expandable Pattern Casting（EPC）Pin Rail

Shang Runqi; Qu Yinhu; Cheng Xiaole

doi:10.15980/j.tzzz.2015.10.023

Views : 0 下载量: 94 CSCD: 0

Export
Share
Collection
Album

Fracture Failure Analysis and Prevention of Expandable Pattern Casting（EPC）Pin Rail
Vol. 35, Issue 10, Pages: 1083-1085(2015)
Published： 2015 ，
DOI： 10.15980/j.tzzz.2015.10.023

扫描看全文

[1]尚润琪,屈银虎,成小乐.消失模铸造销轨的断裂失效分析及预防[J].特种铸造及有色合金,2015,35(10):1083-1085.

Shang Runqi, Qu Yinhu, Cheng Xiaole. Fracture Failure Analysis and Prevention of Expandable Pattern Casting（EPC）Pin Rail. [J]. Special Casting & Nonferrous Alloys 35(10):1083-1085(2015)
[1]尚润琪,屈银虎,成小乐.消失模铸造销轨的断裂失效分析及预防[J].特种铸造及有色合金,2015,35(10):1083-1085. DOI： 10.15980/j.tzzz.2015.10.023.

Shang Runqi, Qu Yinhu, Cheng Xiaole. Fracture Failure Analysis and Prevention of Expandable Pattern Casting（EPC）Pin Rail. [J]. Special Casting & Nonferrous Alloys 35(10):1083-1085(2015) DOI： 10.15980/j.tzzz.2015.10.023.

摘要

利用宏观及微观断口分析、成分分析、力学性能测试对消失模铸造生产的ZG35CrMnSi钢销轨断裂进行失效分析。结果显示

ZG35CrMnSi钢销轨断裂的宏观组织和显微组织含有大量的夹渣

C、Si及Mn超出标准成分上限较多

塑性、韧性不足

从而导致ZG35CrMnSi钢销轨成批脆性断裂。在采用低密度的EPS-PMMA或者PMMA制作模样

采用空心的模样结构或改用砂型铸造工艺

并严格控制该铸件的化学成分

减少夹渣

提高其塑性和韧性

避免脆性断裂。

Abstract

Fracture failure of ZG35 CrMnSi steel pin rail by EPC was analyzed by macro-scope fractography

microanalysis for fracture

chemical analysis

mechanical properties.The results show that the macro or microstructure of pin rail fracture has plenty of slag inclusion

and chemical compositions exceed upper limit of the standard

resulting in the low plasticity and toughness

which lead to the brittle fracture of ZG35 CrMnSi steel pin rail.It is suggested that EPS-PMMA or PMMA is used as the EPC mold

and the hollow mold is used instead of solid mold

or sand casting process must be used instead of EPC.Meanwhile

the chemical composition of castings must be controlled strictly within specification to reduce the slag inclusion and improve the plasticity and toughness.