Effects of Mould Temperature on Microstructure and Tensile Properties of in situ Thixoformed Si<sub>p</sub>/ZA27 Composite

Wang Bo; Chen Tijun; Zhang Jinyu

doi:10.15980/j.tzzz.2015.09.019

Views : 0 下载量: 66 CSCD: 1

Export
Share
Collection
Album

Effects of Mould Temperature on Microstructure and Tensile Properties of in situ Thixoformed Si_p/ZA27 Composite
Vol. 35, Issue 9, Pages: 962-966(2015)
Published： 2015 ，
DOI： 10.15980/j.tzzz.2015.09.019

扫描看全文

[1]王博,陈体军,张金雨.模具温度对Si_p/ZA27复合材料组织及性能的影响[J].特种铸造及有色合金,2015,35(09):962-966.

Wang Bo, Chen Tijun, Zhang Jinyu. Effects of Mould Temperature on Microstructure and Tensile Properties of in situ Thixoformed Si_p/ZA27 Composite. [J]. Special Casting & Nonferrous Alloys 35(9):962-966(2015)
[1]王博,陈体军,张金雨.模具温度对Si_p/ZA27复合材料组织及性能的影响[J].特种铸造及有色合金,2015,35(09):962-966. DOI： 10.15980/j.tzzz.2015.09.019.

Wang Bo, Chen Tijun, Zhang Jinyu. Effects of Mould Temperature on Microstructure and Tensile Properties of in situ Thixoformed Si_p/ZA27 Composite. [J]. Special Casting & Nonferrous Alloys 35(9):962-966(2015) DOI： 10.15980/j.tzzz.2015.09.019.

摘要

研究了模具温度对触变成形Sip/ZA27复合材料组织及力学性能的影响。结果表明

随着模具温度升高

锭料的凝固速率变慢

初生α-Al颗粒尺寸和体积分数增大;而且初生α-Al颗粒中Zn元素的含量增加;此外

Si颗粒的团聚倾向变得严重。通过对试样的力学性能进行比较可知

最佳的模具温度为200℃

此时的抗拉强度和伸长率分别达到382 MPa和1.17%。而且随着模具温度的增加

断裂机制发生转变。

Abstract

Effects of mould temperature on microstructure and tensile properties of in situ thixoformed Sip/ZA27 composites were investigated.The results indicate that with the mould temperature increases

the solidification rate of ingot is decreased

and the size and fraction of the primaryα-Al particles are increased.Moreover

Zn conent in the primary particles is increased.In addition

the aggregation tendency of Si particles tends to become serious.Based on tensile properties testing

the optimal mould temperature is 200℃

where the tensile strength and elongation reach up to 382 MPa and 1.17%

respectively.Moreover

the fracture mode of the thixoformed composites is transformed with the mould temperature increase.