Effects of Drawing Process on Properties of Directional Solidification Cu-Ag Conduct Wires

Feng Cunli; Qin Fangli; Jie Mingshan; Wu Guoqi; Liu Guanglin; Li Lei

doi:10.15980/j.tzzz.2015.08.031

Views : 0 下载量: 202 CSCD: 3

Export
Share
Collection
Album

Effects of Drawing Process on Properties of Directional Solidification Cu-Ag Conduct Wires
Vol. 35, Issue 8, Pages: 893-896(2015)
Published： 2015 ，
DOI： 10.15980/j.tzzz.2015.08.031

扫描看全文

[1]封存利,秦芳莉,介明山,武国旗,刘光林,李雷.拉拔工艺对定向凝固Cu-Ag合金导线性能的影响[J].特种铸造及有色合金,2015,35(08):893-896.

Feng Cunli, Qin Fangli, Jie Mingshan, et al. Effects of Drawing Process on Properties of Directional Solidification Cu-Ag Conduct Wires. [J]. Special Casting & Nonferrous Alloys 35(8):893-896(2015)
[1]封存利,秦芳莉,介明山,武国旗,刘光林,李雷.拉拔工艺对定向凝固Cu-Ag合金导线性能的影响[J].特种铸造及有色合金,2015,35(08):893-896. DOI： 10.15980/j.tzzz.2015.08.031.

Feng Cunli, Qin Fangli, Jie Mingshan, et al. Effects of Drawing Process on Properties of Directional Solidification Cu-Ag Conduct Wires. [J]. Special Casting & Nonferrous Alloys 35(8):893-896(2015) DOI： 10.15980/j.tzzz.2015.08.031.

摘要

采用水平连续定向凝固法

制备了16 mm的不同Ag含量的Cu-Ag合金杆

通过多道次冷拉拔

制备了0.12mm的Cu-Ag合金导线

研究了Ag含量和拉拔变形对Cu-Ag合金的抗拉强度、伸长率与电导率的影响。结果表明

定向凝固杆具有纵向连续柱状晶及良好的伸长率

适合拉拔微细线材。随后采用再结晶退火工艺

提高了合金的伸长率

并成功试制了电导率达58.00 MS/m、抗拉强度为300 MPa、伸长率为23%的Cu-Ag合金细线。

Abstract

ф16mm Cu-Ag alloy rod billets with different Ag content were prepared by horizontal continuous directional solidification method.The Cu-Ag alloy wire with 0.12 mm in diameter was produced with many passes of cold drawing.The mechanical properties and electrical conductivity of Cu-Ag wires were tested.Effects of Ag content and drawing deformation on the tensile strength

elongation and electric conductivity of Cu-Ag wires were examined.The results show that the directional solidification rod billet exhibits continuous columnar crystal textures along the longitudinal direction

which results in excellent elongation performance.Therefore

it is very suitable for drawing fine wires.Finally

wires’ elongation is increased by the recystallization annealing processing.Cu-Ag alloy fine wires with 58.00MS/m conductivity

300 MPa strength and 23% elongation were produced successfully.