Effects of Pouring Temperatures on Microstructure Evolution of Mg-10Sm Alloy

Li Daquan; Wang Guangzong; Liang Xiaokang; Xu Xiaojing; Zhu Qiang

doi:10.15980/j.tzzz.2015.03.007

Views : 0 下载量: 90 CSCD: 1

Export
Share
Collection
Album

Effects of Pouring Temperatures on Microstructure Evolution of Mg-10Sm Alloy
Vol. 35, Issue 3, Pages: 248-251(2015)
Published： 2015 ，
DOI： 10.15980/j.tzzz.2015.03.007

扫描看全文

[1]李大全,王光宗,梁小康,许小静,朱强.浇注温度对Mg-10Sm合金凝固组织的影响[J].特种铸造及有色合金,2015,35(03):248-251.

Li Daquan, Wang Guangzong, Liang Xiaokang, et al. Effects of Pouring Temperatures on Microstructure Evolution of Mg-10Sm Alloy. [J]. Special Casting & Nonferrous Alloys 35(3):248-251(2015)
[1]李大全,王光宗,梁小康,许小静,朱强.浇注温度对Mg-10Sm合金凝固组织的影响[J].特种铸造及有色合金,2015,35(03):248-251. DOI： 10.15980/j.tzzz.2015.03.007.

Li Daquan, Wang Guangzong, Liang Xiaokang, et al. Effects of Pouring Temperatures on Microstructure Evolution of Mg-10Sm Alloy. [J]. Special Casting & Nonferrous Alloys 35(3):248-251(2015) DOI： 10.15980/j.tzzz.2015.03.007.

摘要

在不同浇注温度下浇注Mg-10Sm合金

研究了浇注温度对Mg-10Sm合金凝固组织的影响。结果表明

随着浇注温度的降低

试样外部粗大柱状树枝晶区逐渐缩小

浇注温度在700℃及以下

外部柱状晶区消失

转化为细小等轴晶;试样心部粗大树枝晶逐渐细化并转变为细小的等轴晶。二次枝晶间距随着浇注温度的降低逐渐减小。浇注温度对合金共晶相体积分数、共晶相分布以及共晶相形貌没有明显的影响。

Abstract

Effects of different pouring temperatures such as 750

730

700

675 and 650 ℃ on microstructure evolution of metal mold casting Mg-10 Sm alloy were investigated.The results reveal that the grain size of the Mg-10 Sm alloy is significantly refined

and the microstructure is transformed from big columnar and quiaxed dentrite grains to small equiaxed grains with decreasing in the pouring temperatures.The second dendrite arm spacing（SDAS）is gradually decreased with decreasing in the pouring temperatures.Effects of pouring temperature on the eutectic volume fraction

eutectic distribution and eutectic morphology can be ignored.