Effect of Electromagnetic Stirring on Equiaxial Crystal Ratio in Stainless Steel
Vol. 34, Issue 9, Pages: 955-957(2014)
Published： 2014 ，
DOI： 10.15980/j.tzzz.2014.09.061

扫描看全文

[1]吴斌,陈兴润.电磁搅拌对不锈钢连铸坯等轴晶率的影响[J].特种铸造及有色合金,2014,34(09):955-957.

Wu Bin, Chen Xingrun. Effect of Electromagnetic Stirring on Equiaxial Crystal Ratio in Stainless Steel. [J]. Special Casting & Nonferrous Alloys 34(9):955-957(2014)
[1]吴斌,陈兴润.电磁搅拌对不锈钢连铸坯等轴晶率的影响[J].特种铸造及有色合金,2014,34(09):955-957. DOI： 10.15980/j.tzzz.2014.09.061.

Wu Bin, Chen Xingrun. Effect of Electromagnetic Stirring on Equiaxial Crystal Ratio in Stainless Steel. [J]. Special Casting & Nonferrous Alloys 34(9):955-957(2014) DOI： 10.15980/j.tzzz.2014.09.061.

摘要

分析了在工业试验条件下

电磁搅拌对430不锈钢、409L不锈钢和2205双相不锈钢连铸坯等轴晶率的影响。结果表明

施加电磁搅拌后

3个钢种的等轴晶率比不施加电磁搅拌都有明显增加

各个钢种的等轴晶率跟钢种特性有关。

Abstract

Effects of electromagnetic stirring on equiaxial crystal ratio in 430 ferritic stainless steel、409L ferritic stainless steel and 2205 duplex stainless steel slab were analyzed under industry test.The results show that the equiaxial crystal ratios in slabs with electromagnetic stirring are obviously increased compared with no-EMS

and the equiaxial crystal ratios in slabs are all different

which is related to the characteristics of stainless steel grade.