Effect of Nano TiN/Ti Refiner on As-cast Microstructure and Properties of 7050 Aluminium Alloy
Vol. 34, Issue 4, Pages: 341-345(2014)
Published： 2014 ，
DOI： 10.15980/j.tzzz.2014.04.008

扫描看全文

[1]李欣蔚,肖亚婷,李冰,干路,罗强,蔡启舟.纳米TiN/Ti细化剂对7050合金组织和性能的影响[J].特种铸造及有色合金,2014,34(04):341-345.

Li Xinwei, Xiao Yating, Li Bing, et al. Effect of Nano TiN/Ti Refiner on As-cast Microstructure and Properties of 7050 Aluminium Alloy. [J]. Special Casting & Nonferrous Alloys 34(4):341-345(2014)
[1]李欣蔚,肖亚婷,李冰,干路,罗强,蔡启舟.纳米TiN/Ti细化剂对7050合金组织和性能的影响[J].特种铸造及有色合金,2014,34(04):341-345. DOI： 10.15980/j.tzzz.2014.04.008.

Li Xinwei, Xiao Yating, Li Bing, et al. Effect of Nano TiN/Ti Refiner on As-cast Microstructure and Properties of 7050 Aluminium Alloy. [J]. Special Casting & Nonferrous Alloys 34(4):341-345(2014) DOI： 10.15980/j.tzzz.2014.04.008.

摘要

采用高能球磨法制备了纳米TiN/Ti复合晶粒细化剂

研究了该细化剂对7050铝合金铸态组织和性能的影响。结果表明

0.2%的复合细化剂对7050铝合金细化效果明显优于纯Ti细化剂

可使合金平均晶粒尺寸由未添加细化剂的105.5μm细化至83.5μm

组织中的第二相细小、分布较均匀。添加了复合细化剂的7050铝合金铸态抗拉强度由未添加细化剂的187.8MPa提高至220.8MPa

硬度（HB）由未添加细化剂时的97.63提高至102.7。

Abstract

A kind of Ti cladding nano-sized TiN（TiN/Ti）composite grain refiner was prepared by high energy ball milling.Effects of the grain refiner prepared on the as-cast microstructure and properties of the 7050aluminum alloy were approached.The results show that TiN/Ti grain refiner is superior to pure Ti in refining grain of 7050aluminum alloy obviously

and the average grain size in the 7050aluminum alloy is refined from 105.5μm to 83.5μm

meanwhile

second phases is well refined with uniform distribution in the microstructure.Tensile strength and hardness of 7050aluminum alloy with TiN/Ti grain refiner are improved from 187.8MPa to 220.8MPa and from HB97.63to HB102.7

respectively.