Preparation of Composites for High Power Intensity Aluminum Piston Ring and its Wear Resistance
Vol. 33, Issue 12, Pages: 1175-1178(2013)
Published： 2013 ，
DOI： 10.15980/j.tzzz.2013.12.004

扫描看全文

[1]侯林冲,彭银江,周灵展,张广明,徐英.高功率密度铝活塞环岸复合材料制备工艺与耐磨性能[J].特种铸造及有色合金,2013,33(12):1175-1178.

Hou Linchong, Peng Yinjiang, Zhou Lingzhan, et al. Preparation of Composites for High Power Intensity Aluminum Piston Ring and its Wear Resistance. [J]. Special Casting & Nonferrous Alloys 33(12):1175-1178(2013)
[1]侯林冲,彭银江,周灵展,张广明,徐英.高功率密度铝活塞环岸复合材料制备工艺与耐磨性能[J].特种铸造及有色合金,2013,33(12):1175-1178. DOI： 10.15980/j.tzzz.2013.12.004.

Hou Linchong, Peng Yinjiang, Zhou Lingzhan, et al. Preparation of Composites for High Power Intensity Aluminum Piston Ring and its Wear Resistance. [J]. Special Casting & Nonferrous Alloys 33(12):1175-1178(2013) DOI： 10.15980/j.tzzz.2013.12.004.

摘要

针对高功率密度柴油机铝活塞性能要求

活塞环岸采用Al2O3陶瓷纤维增强铝基复合材料

对复合材料结构设计、纤维预处理、预制件制备、挤压铸造成形工艺和耐磨性能进行了研究。经过预处理后的氧化铝纤维其长短搭配合理

渣球含量少

对纤维预制件的成形有利。对挤压铸造工艺进行了优化

采用优化后的工艺制备的活塞其纤维增强部位的界面结合良好

复合材料的显微组织细密、纤维分布均匀、渣球数量少。氧化铝纤维增强铝基复合材料的耐磨性优于高镍铸铁。

Abstract

Al2O3 ceramic fibre reinforced aluminum matrix composites were used to produce piston ring to meet the requirement of piston performance of high power intensity diesel engine.The structure design

fibre pre-treatment

preparation of pre-form and squeezing casting parameters as well as wear resistance of the composites were investigated.The results indicate that Al2O3 fiber pre-treated exhibits rational constituent with few slag ball content

which is beneficial for the forming of fibre pre-form.The squeezing parameters were optimized

and the desirable interfacial bonding can be observed in fibre reinforced position of piston with the optimized squeezing parameters

and fine and compact microstructure in the composites with uniformly distributed fibre and little inclusion are observed too.Wear resistance of the composites ring prepared is superior to that of high Ni cast iron.