Microstructures and Properties of Squeezing Casting 10SiC<sub>P</sub> Reinforced A356 Composites with Different Particle Size

Zhu Gang; Dong Puyun; Zhao Haidong

doi:10.15980/j.tzzz.2013.10.005

Views : 0 下载量: 178 CSCD: 4

Export
Share
Collection
Album

Microstructures and Properties of Squeezing Casting 10SiC_P Reinforced A356 Composites with Different Particle Size
Vol. 33, Issue 10, Pages: 960-963(2013)
Published： 2013 ，
DOI： 10.15980/j.tzzz.2013.10.005

扫描看全文

[1]朱刚,董普云,赵海东.SiC_p粒度对挤压铸造10SiC_p/A356复合材料组织和性能的影响[J].特种铸造及有色合金,2013,33(10):960-963.

Zhu Gang, Dong Puyun, Zhao Haidong. Microstructures and Properties of Squeezing Casting 10SiC_P Reinforced A356 Composites with Different Particle Size. [J]. Special Casting & Nonferrous Alloys 33(10):960-963(2013)
[1]朱刚,董普云,赵海东.SiC_p粒度对挤压铸造10SiC_p/A356复合材料组织和性能的影响[J].特种铸造及有色合金,2013,33(10):960-963. DOI： 10.15980/j.tzzz.2013.10.005.

Zhu Gang, Dong Puyun, Zhao Haidong. Microstructures and Properties of Squeezing Casting 10SiC_P Reinforced A356 Composites with Different Particle Size. [J]. Special Casting & Nonferrous Alloys 33(10):960-963(2013) DOI： 10.15980/j.tzzz.2013.10.005.

摘要

进行了SiCp为10μm和150μm增强A356铝基复合材料的搅拌制备及75MPa下的挤压铸造

研究了颗粒尺寸对挤压铸造复合材料微观组织和力学性能的影响。结果表明

挤压铸造SiCp/A356铸件内部缺陷少、致密度高

颗粒团聚倾向小;铸态下

SiCp为10μm的10SiCp/A356复合材料的抗拉强度、硬度和伸长率均高于SiCp为150μm的10SiCp/A356的。T6热处理后

两者的力学性能均得到显著提高

SiCp为150μm的抗拉强度和硬度高于SiCp为10μm的。

Abstract

10%SiCP with 10μm and 150μm in size reinforced A356metalmatrix composites were fabricated by stirring casting and then direct squeeze casting process under 75MPa.Effects of particle size on the microstructures and mechanical properties of the castings were investigated.The results show that compared to 10μm SiCp/A356composites

squeezing casting 150μm SiCp/A356composites exhibit less internal defects and higher density as well as lower tendency of particle cluster.The as-cast tensile strength

hardness and elongation of 10μm SiCp/A356composites are superior to those of 150μm SiCp/A356composites.After T6heat treatment

the mechanical properties of both 150μm SiCp/A356and 10μm SiCp/A356composites are increased greatly

however

tensile strength and hardness of 150μm SiCp/A356composites are higher than those of 10μm SiCp/A356composites.

关键词

金属基复合材料挤压铸造微观组织

Keywords

Metal Matrix CompositesSqueeze CastingMicrostructures

references

Alert me when the article has been cited

提交

Effects of Particle Size on Microstructures and Properties of the 10SiC_p/6061 Composites by Squeezing Casting Process

Mechanical properties ofB₄C_p/2024Al composites prepared by squeeze casting

Microstructure and Properties of SiC_w/Al Composites Fabricated by Squeeze Casting Method

Friction and Wear Behavior of Squeeze-Cast 10SiC_p/A356 Composites

Squeeze Casting Process of Aluminum Alloy Inclined Tube

Microstructures and Properties of Squeezing Casting 10SiCP Reinforced A356 Composites with Different Particle Size

DOI： 10.15980/j.tzzz.2013.10.005

摘要

Abstract

关键词

Keywords

references

Microstructures and Properties of Squeezing Casting 10SiC_P Reinforced A356 Composites with Different Particle Size