Effect of Cu,Si and Ti on Microstructure and Properties for a Zinc-aluminum Alloy

Chi Changzhi; Li Shixin; Zhang Lei

doi:10.15980/j.tzzz.2013.09.028

Views : 0 下载量: 204 CSCD: 2

Export
Share
Collection
Album

Effect of Cu,Si and Ti on Microstructure and Properties for a Zinc-aluminum Alloy
Vol. 33, Issue 9, Pages: 878-880(2013)
Published： 2013 ，
DOI： 10.15980/j.tzzz.2013.09.028

扫描看全文

[1]迟长志,李世欣,张磊.Cu、Si、Ti对锌铝合金组织与性能的影响[J].特种铸造及有色合金,2013,33(09):878-880.

Chi Changzhi, Li Shixin, Zhang Lei. Effect of Cu,Si and Ti on Microstructure and Properties for a Zinc-aluminum Alloy. [J]. Special Casting & Nonferrous Alloys 33(9):878-880(2013)
[1]迟长志,李世欣,张磊.Cu、Si、Ti对锌铝合金组织与性能的影响[J].特种铸造及有色合金,2013,33(09):878-880. DOI： 10.15980/j.tzzz.2013.09.028.

Chi Changzhi, Li Shixin, Zhang Lei. Effect of Cu,Si and Ti on Microstructure and Properties for a Zinc-aluminum Alloy. [J]. Special Casting & Nonferrous Alloys 33(9):878-880(2013) DOI： 10.15980/j.tzzz.2013.09.028.

摘要

通过正交试验方法

利用金相显微镜、扫描电镜、冲击试验等研究了Cu、Si、Ti对锌铝合金组织与性能的影响

确定了优化成分。结果表明

Zn-4Al合金最优化的成分为Zn-4Al-1.25Cu-0.04Ti

其冲击韧度为85.5J/cm2。Zn-Al合金的共晶组织耐冲击性能最差;Si严重降低冲击性能

Ti和Cu都可以细化合金组织和提高力学性能。

Abstract

Effects of Cu

Si and Ti on microstructure and properties of Zn-Al alloy which was optimized by orthogonal test were investigated with optical microscopy

scanning electron microscopy

impact testing and so on.The results show that the optimum alloy composition of the Zn-4Al alloy is Zn-4Al-1.25 Cu-0.04Ti

and its impact toughness is 85.5J/cm2.The Zn-Al eutectic alloy has the worst impact resistance.Si addition can deteriorate seriously the impact properties.Ti and Cu can refine the microstructure in the Zn alloy and improve the mechanical properties.