Continuous Cast Forming Machine with Vertical Core-Filling for Copper Cladding Aluminum Composite Bars
Vol. 33, Issue 3, Pages: 265-268(2013)
Published： 2013 ，
DOI： 10.15980/j.tzzz.2013.03.034

扫描看全文

[1]张建宇,王屹峰,万长清,曾祥勇,蔡鹏,吴春京.铜包铝复合扁排立式充芯连铸设备的研制[J].特种铸造及有色合金,2013,33(03):265-268.

Zhang Jianyu1, Wang Yifeng2, Wan Changqing1, et al. Continuous Cast Forming Machine with Vertical Core-Filling for Copper Cladding Aluminum Composite Bars. [J]. Special Casting & Nonferrous Alloys 33(3):265-268(2013)
[1]张建宇,王屹峰,万长清,曾祥勇,蔡鹏,吴春京.铜包铝复合扁排立式充芯连铸设备的研制[J].特种铸造及有色合金,2013,33(03):265-268. DOI： 10.15980/j.tzzz.2013.03.034.

Zhang Jianyu1, Wang Yifeng2, Wan Changqing1, et al. Continuous Cast Forming Machine with Vertical Core-Filling for Copper Cladding Aluminum Composite Bars. [J]. Special Casting & Nonferrous Alloys 33(3):265-268(2013) DOI： 10.15980/j.tzzz.2013.03.034.

摘要

设计和制造了一台制备铜包铝复合扁排的立式充芯连铸试验设备

该设备的特点是在高度方向上设置上下两个加热坩埚分别熔化铜和铝;外层铜管在结晶器中首先形成

铝液随之通过充芯管充填到铜管中

铜、铝界面通过互扩散实现冶金结合。利用此设备

成功地连铸出铜层厚度为2mm

芯部铝厚度为10mm

宽为60mm的铜包铝复合扁排。

Abstract

A new continuous core-filling casting machine for copper cladding aluminum composite bars was designed and produced.The machine installed the upper and bottom graphite crucibles in the vertical direction for heating inner core of aluminum and the outer layer of copper.During continuous casting

copper tube was formed in the crystallizer continuously firstly

then liquid aluminum was injected into the copper tube through mandrel.Finally

the metallurgical bonded layer was formed by inter-diffusion between copper and aluminum.The copper cladding aluminum composite bars with the core thickness of 10 mm and the sheath thickness of 2 mm and the width of 60 mm were fabricated successfully by the machine.